Friction Stir Welding (FSW) was used to perform a Design of Experiment (DOE) to determine the welding parameters effects on yielding consistent mechanical properties across the length of the weld. The travel speed was varied across set forge force and RPM conditions, to find a dataset that will yield consistent mechanical properties independent of the travel speed. Six different welds were completed on two different aluminum panels, the advancing side being Aluminum alloy 2195-T8 at a thickness of .350”, with the retreating side being Aluminum alloy 2219-T851 with a gauge thickness of .360”. A Left-hand Right-hand self-reacting pin tool was used for each weld. The mechanical properties of interest are the Ultimate Tensile Strength, Yield Strength, Elasticity and Hardness. The strengths were evaluated by tensile testing, with the Elasticity being measure post break. Specimens were then polished where macrograph and micrograph analysis was completed. Micro-hardness testing was then completed on the weld nuggets.
| Identifer | oai:union.ndltd.org:uno.edu/oai:scholarworks.uno.edu:td-3509 |
| Date | 09 August 2017 |
| Creators | Marrero, Robert L, Jr |
| Publisher | ScholarWorks@UNO |
| Source Sets | University of New Orleans |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | University of New Orleans Theses and Dissertations |
Page generated in 0.0022 seconds