Evidence is reported for the formation of carbon-containing contamination products at the copper-tungsten (Cu-W) interface during the metal organic chemical vapor deposition (MOCVD) of copper on tungsten. Cu(II)bishexafluoroacetylacetonate [Cu(hfac)_2] was physisorbed onto lightly oxidized tungsten (WO_x) at 115K, under ultra-high vacuum conditions, and then annealed sequentially to higher temperatures. Copper reduction was observed by 320K. Carbonaceous and carbidic contamination of the WO_x surface was observed, even after sample warming to 625K in UHV. The results indicate that low temperature MOCVD of Cu may be possible, but interfacial contamination from the organic ligand fragmentation is a major concern.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc500726 |
Date | 05 1900 |
Creators | Welton, Theresa E. (Theresa Eilene) |
Contributors | Kelber, Jeffry Alan, 1952-, Daugherty, Kenneth E. |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | iv, 32 leaves : ill., Text |
Rights | Public, Copyright, Copyright is held by the author, unless otherwise noted. All rights reserved., Welton, Theresa E. (Theresa Eilene) |