The influence of Two-Step Sintering (TSS) process on the final microstructure of oxide ceramics materials with two different crystal structures was studied. Tetragonal zirconia (stabilized with 3mol%Y2O3, particle size 90nm and 140nm ) and cubic zirconia (8mol%Y2O3, 70nm) powders were cold isostatically pressed and pressure less sintered with different heating schedules. The microstructures achieved with TSS method were compared with microstructures achieved with conventional Single-Step Sintering schedule (SSS). The results showed that the efficiency of the TSS of these oxide ceramics was more dependent on their crystal structure than on their particle size and green body microstructure. The method of TSS brought only negligible improvement of the microstructure of tetragonal zirconia ceramics. On the other hand, TSS was successful in the sintering of cubic zirconia ceramics; it led to a decrease in grain size by a factor of 2.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:228739 |
| Date | January 2009 |
| Creators | Žalud, Pavel |
| Contributors | Trunec, Martin, Maca, Karel |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0022 seconds