Cubic Zn1-xMgxO (c-Zn1-xMgxO) thin films have opened the deep ultraviolet (DUV) spectrum to exploration by oxide optoelectronic devices. These extraordinary films are readily wet-etch-able, have inversion symmetric lattices, and are made of common and safe constituents. They also host a number of new exciting experimental and theoretical challenges. Here, the relation between growth conditions of the c-Zn1-xMgxO film and performance of fabricated ultraviolet (UV) sensors is investigated. Plasma-Enhanced Molecular Beam Epitaxy was used to grow Zn1-xMgxO thin films and formation conditions were explored by varying the growth temperature, Mg source flux, oxygen flow rate, and radio-frequency (RF) power coupled into the plasma. Material review includes the effect of changing conditions on the film’s optical transmission, surface morphology, growth rate, crystalline phase, and stoichiometric composition. Oxygen plasma composition was investigated by spectroscopic analysis under varying oxygen flow rate and applied RF power and is correlated to device performance. Ni/Mg/Au interdigitated metalsemiconductor-metal detectors were formed to explore spectral responsivity and UV-Visible rejection ratio (RR). Zn1-xMgxO films ranged in Mg composition from x = 0.45 - 1.0. Generally, x increased with increasing substrate temperature and Mg source flux, and decreased with increasing oxygen flow rate and RF power. Increasing x was correlated with decreased peak responsivity intensity and increased RR. Device performance was improved by increasing the ratio of O to O+ atoms and minimizing O2 + in the plasma. Peak responsivity as high as 500 A/W was observed in visible-blind phase-segregated Zn1-xMgxO devices, while cubic iv phase solar-blind devices demonstrated peak responsivity as high as 12.6 mA/W, and RR of three orders of magnitude. Optimal conditions are predicted for the formation of DUV Zn1- xMgxO sensors
| Identifer | oai:union.ndltd.org:ucf.edu/oai:stars.library.ucf.edu:etd-3711 |
| Date | 01 January 2013 |
| Creators | Boutwell, Ryan |
| Publisher | STARS |
| Source Sets | University of Central Florida |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Electronic Theses and Dissertations |
Page generated in 0.0017 seconds