Study on the treatment of PCB Wastewater by Ferrite Process combined with Fenton¡¦s Method and UV/H2O2

Biological and physical chemistry treatment methods always are used to remove COD of organic wastewater contains PCB. The effect is not obvious when the compositions of pollutant are too refractory or complicated. The primary treatment method of wastewater containing copper is chemical coagulation/sedimentation and its disadvantage is producing a large of sludge.
The objective of this study, using two combinative method of UV/H2O2-Ferrite Process and Fenton-Ferrite Process, is to remove organic compounds and heavy metal in real wastewater. Not only supernatant liquid could meet the standard of discharge wastewater but also produce general(non-hazardous) industrial wastes of heavy metal.
The primary operation condition of Fenton and UV/H2O2 process, was ferrous ion and hydrogen peroxide concentration, pH, reaction time, and chemical dosing, searching best operation condition to combine with Ferrite Process. Operation of Fenton and UV/H2O2 process under acid condition (pH=2) and neutral condition (pH=8) showed the best operation condition of Fenton and UV/H2O2. The removal decreased when the dose of hydrogen peroxide was added too more or too less.
As Fenton and UV/H2O2 process test finished, Ferrite Process is next used for treatment of heavy metal wastewater; Ferrite Process conducted as three stages and the operation conditions were controlled with temperature, pH and the ratio of Fe/M mole. The results showed that the best removal of treatment of copper containing wastewater by Ferrite Process achieved when the ratio of Fe/M mole was at 10. Treatment of PCB industrial real wastewater by Fenton-Ferrite Process and UV/H2O2-Ferrite Process which combined with Fenton, UV/H2O2 and Ferrite Process. The supernatant liquid containing organic compounds and heavy metal both could meet the standards of discharge wastewater and the sludge was judged with general(non-hazardous) wastes. The characteristic of the sludge were the diameter lattice less 100 nm and with magnetism and to develop recovery and utilization in a further work.

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0628106-220508
Date28 June 2006
CreatorsChen, Chin-Yang
Contributorsnone, NONOE, none
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageCholon
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0628106-220508
Rightswithheld, Copyright information available at source archive

Page generated in 0.0021 seconds