Mechanism and Mechanical Performance of AS4/PEEK Composite Laminates at Elevate Temperature Subjected to impact

ABSTRACT
AS4/PEEK (APC-2) is a thermoplastic composite materials consisting of polyether-ether-ketone (PEEK) reinforced with AS4 carbon fibers. APC-2 has been widely used in many weight critical applications because of high specific strength and stiffness, good corrosion resistance, good formability and high temperature durability. However, the susceptibility of composite materials to damage result from low-velocity impacts (for example, from dropped tools, runway stones or hailstones) is a major problem. Low-velocity impact induces internal damage in the composite laminate without any visible sign on the surface, but it is result in a loss of laminate strength. This paper is aimed to investigate the mechanism and mechanical performance of [0/90] and [0/+45/90/-45] laminates subjected to Drop-Weight Impact by a cylindro-conical, a cylindro-hemisphere and a cylindrical impactor tip at temperature of 25¢J, 75¢Jand 125¢J.
The study of impact response and post impact strength of composite laminates subjected to low velocity impact shows that the failure mechanism is predominantly delamination and fiber breakage.
Generalizing the results of experiment, we can conclude that an impactor with a small nose (cylindro-conical) induces a larger impact-induced damage than one with a large nose (cylindrical), as well as a greater degree of fiber breakage. But for the reduction of post-impact strength, the cylindro-hemisphere impcator induces the most reduction of strength than the cylindro-conical and the cylindrical impactors. The post-impact residual strength of [0/90] specimens is higher than [0/+45/90/-45] specimens. But, [0/+45/90/-45] specimens are better to resist the impact effect. As for the effect of elevated temperature, we found that when the temperature increases, the damage extent reduces slowly.
Keywords: composite, low-velocity impact, temperature effect, young's modulus, ultimate strength

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0710100-123351
Date10 July 2000
CreatorsZheng, Chuan-Her
ContributorsMing Chen, Ming-Hwa R Jen, Huang-Kuang Kung
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageCholon
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0710100-123351
Rightsunrestricted, Copyright information available at source archive

Page generated in 0.002 seconds