This diploma thesis describes properties of ultra-fine grain Cu prepared via ECAP procedure. The influence of fatigue loading with positive mean stress on S-N curve (i.e. fatigue life), cyclic plastic behaviour and grain size was investigated. It was found that tensile mean stress leads to shorter lifetime in comparison with fatigue loading with zero mean stress. During main part of the lifetime, significant hardening of UFG Cu was observed. There is no distinct effect on microstructural orientation and stability.