Previous issue date: 2009 / Esse trabalho é parte integrante de um estudo que visa a aplicabilidade
da técnica ultra-sônica no domínio da freqüência para a caracterização não
destrutiva de pastilhas combustíveis cerâmicas, que é de grande interesse
devido a preocupação com a segurança e eficácia na indústria nuclear.
Nesse Trabalho foram analisadas as alterações nos espectros de
freqüência, gerados pela passagem de um pulso ultra-sônico através de
pastilhas cerâmicas à base de óxido de alumínio (Al2O3). Utilizando a técnica
ultra-sônica no domínio da freqüência, juntamente com análise micro-estrutural
das pastilhas, através do microscópio eletrônico de varredura, foi possível
associar as características do material inspecionado ao seu respectivo espectro
de freqüência. A caracterização foi feita em 40 pastilhas de Alumina
sinterizadas às temperaturas de 1150, 1400, 1480, 1540 e 1580°C com
porosidades, medidas pelo método de Arquimedes, variando de 5,09% a
37,3%.
Os resultados obtidos mostram que esta técnica ultra-sônica é eficaz na
determinação da micro-estrutura de pastilhas cerâmicas de Alumina podendo
ser aplicado na caracterização de outros materiais porosos em uma linha de
produção, onde o formato do espectro de freqüência gerado pela estrutura do
material pode determinar se as pastilhas se enquadram nas especificações
requeridas. / This work is part of a study to the applicability of ultrasonic technique in
the frequency domain for non-destructive characterization of ceramic pellets
fuel, which is of great interest because of concern about the safety and efficacy
in the nuclear industry.
In this work it was analised if there were changes in frequency spectrum,
generated by the traveling of an ultrasonic pulse through ceramic pellets of
aluminum oxide (Al2O3). Using the ultrasonic technique in the frequency
domain, together with micro-structural analysis of pellets by scanning electron
microscope, it was possible to associate the characteristics of the material
inspected with its respectives frequency spectrum. The characterization was
performed on 40 pellets alumina sintered in the temperatures of 1150, 1400,
1480, 1540 and 15800C with porosities, as measured by the Archimedes
method, ranging from 5.09% to 37.3%.
The results show that the ultrasonic technique is effective in determining
the micro-structure of ceramic alumina pellets and can be applied in the
characterization of other porous materials in a production line, where the format
of the frequency spectrum generated by the structure of the material may
determine if the pellets belong the required specifications.
| Identifer | oai:union.ndltd.org:IBICT/oai:carpedien.ien.gov.br:ien/546 |
| Date | 04 1900 |
| Creators | COSTA, Antonio Mario Leal Martins |
| Contributors | SOARES, Maria da Conceição Barbosa Vieira, LAMY, Carlos Alfredo, SOSMAN, Lilian Pantoja, BITTENCOURT, Marcelo de Siqueira Queiroz |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional do IEN, instname:Instituto de Engenharia Nuclear, instacron:IEN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds