An increasing number of engineering components are expected to have fatigue life in the range of 107 - 1010 load cycles. Some examples of such components are found in airplanes, automobiles and high speed trains. For many materials fatigue failures have lately been reported to occur well after 107 load cycles, namely in the Very High Cycle Fatigue (VHCF) range. This finding contradicts the established concept of a fatigue limit, which postulates that having sustained around 107 load cycles the material is capable of enduring an infinite number of cycles provided that the service conditions are unchanged. With the development of modern ultrasonic fatigue testing equipment it became possible to experimentally establish VHCF behaviour of various materials. For many of them the existence of the fatigue limit at 107 load cycles has been proved wrong and their fatigue strength continues to decrease with increasing number of load cycles. High performance steels is an important group of materials used for the components subjected to VHCF. This study explores the VHCF phenomenon using experimental data generated by ultrasonic fatigue testing of selected tool steels. The overall aim is to gain knowledge of VHCF behaviour of some common tool steel grades, while establishing a fundamental understanding of mechanisms for crack development in the very long life regime. The study demonstrates that VHCF cracks in tested steels initiate from microstructural defects like slag inclusions, large carbides or voids. It is established that VHCF life is almost exclusively spent during crack formation at below threshold stress intensity values which results in a unique for VHCF morphology on the fracture surface. Significant attention is devoted in the thesis to the ultrasonic fatigue testing technique, i.e. the validity and applicability of its results. FEM is employed to give an additional perspective to the study. It was used to calculate local stresses at fatigue initiating defects; examine the effect of material damping on ultrasonic stresses; and to evaluate various specimen geometries with respect to resulting stress gradient and maximum stressed material volume.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kau-5877 |
Date | January 2010 |
Creators | Kazymyrovych, Vitaliy |
Publisher | Karlstads universitet, Avdelningen för maskin- och materialteknik, Karlstad : Karlstad University |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Karlstad University Studies, 1403-8099 ; 2010:20 |
Page generated in 0.0017 seconds