Submitted by Edisangela Bastos (edisangela@ufpa.br) on 2018-03-28T16:02:01Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Tese_EfeitosTipoTamanho.pdf: 6130930 bytes, checksum: 6cf79fe54cf5dc4d13c1cb31ff745a78 (MD5) / Approved for entry into archive by Edisangela Bastos (edisangela@ufpa.br) on 2018-04-02T14:53:33Z (GMT) No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Tese_EfeitosTipoTamanho.pdf: 6130930 bytes, checksum: 6cf79fe54cf5dc4d13c1cb31ff745a78 (MD5) / Made available in DSpace on 2018-04-02T14:53:33Z (GMT). No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Tese_EfeitosTipoTamanho.pdf: 6130930 bytes, checksum: 6cf79fe54cf5dc4d13c1cb31ff745a78 (MD5)
Previous issue date: 2004-09-28 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Este trabalho expõe os resultados de um estudo conduzido para avaliar os efeitos do tipo, tamanho e consumo de agregado graúdo no comportamento do concreto de moderada e de alta resistência, e as relações entre a resistência à compressão, resistência à tração, resistência à flexão e a energia de fratura. As misturas de concreto estudadas continham agregados britados de basalto e de granito com dimensões máximas características de 9,5 mm e 19 mm e fração volumétrica no traço entre 0,65 e 0,75. A relação águalaglomerantes variou de 0,35 a 0,50. Nas misturas de alta resistência foi empregado um teor fixo de sílica ativa de dez porcento da massa do cimento de alta resistência inicial e teores adequados de aditivo superplastificante. Foram feitas dezesseis (16) misturas e realizados cento e noventa e dois ensaios mecânicos para medir a resistência à compressão, a resistência à flexão, resistência à tração, módulo de elasticidade e energia de fratura. As propriedades de fratura foram determinadas de acordo com Comitê Técnico 89-FMT e FMC-50 da RILEM. A resistência à compressão do concreto de acordo com os materiais empregados foi de 40 a 60 MPa para os concretos de resistência média e de 70 a 110 MPa, para os concretos de alta resistência. Os resultados mostram que a resistência. à compressão, tração, flexão e a energia de fratura do concreto para uma dada relação águaJaglomerante depende do tipo, dimensões e teor de agregado. Para o concreto de alta resistência o comprimento característico do concreto aumenta com o tamanho do agregado graúdo / This thesis presents the results of the experimental study carried out for considering the
effects of the type, size and amount of coarse aggregate on the behavior of normal and high
strength concretes, and on relationship among the fracture energy and typical mechanical strength
of concrete. The experimental concrete mixtures were made with basalt and granite coarse
aggregates having maximum size particle 9.5 mm e 19 mm and volumetrically fraction in the
mixture ranging from 0.65 to 0.75. The water to cementation materiais ratio ranged from 0.35 to
0.50. The high strength concrete mixtures contained a fixed amount of 10 percent of silica fume
in relation to the weight Portland cement used and a proper addition of superplasticizing agent.
Sixteen (16) concrete batching, and one hundred and ninety two tests were carried out to measure
the mechanical resistance of concrete (compressive strength, flexure strength, spittling tensile
strength, modulus of elasticity) and fracture energy. The fracture properties measured in
agreement of the RILEM test methods. The concrete compressive strength ranged from 40 to 60
MPa, and from 70 to 110 MPa, for moderate and high strength concretes, respectively, depending
on the type of coarse aggregate utilized. The results showed that the concrete resistance
(compressive, flexure, spittling tensile) and fracture energy, at given water to binder ratio, depend
on type, particle dimension and content of coarse aggregate. The characteristic length of
Hülerborg^ fictitions cracks model increases with the variation in the particle dimension of
coarse aggregate.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/9650 |
| Date | 28 September 2004 |
| Creators | POMPEU NETO, Bernardo Borges |
| Contributors | FERREIRA, Itamar, DUCATTI, Vitor Antonio |
| Publisher | Universidade Estadual de Campinas, Programa de Pós-Graduação em Engenharia Mecânica – PPGEM/UNICAMP, UNICAMP, Brasil, Faculdade de Engenharia Mecânica – FEM/UNICAMP |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA, http://repositorio.unicamp.br/handle/REPOSIP/265011 |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0117 seconds