Previous issue date: 2011 / Resumo: Esse trabalho concentra os estudos na investigação das propriedades de resistência a tração e alongamento do compósito de Politetrafluoretileno (PTFE) com 60% de bronze após a substituição do tipo de PTFE utilizado na formulação desse compósito. Atualmente esse compósito utiliza PTFE convencional na formulação e o objetivo é alterar para PTFE modificado. A motivação para essa alteração deveu-se ao fato que o PTFE convencional apresenta disponibilidade limitada dificultando o desenvolvimento dos segmentos que utilizam os compósitos de PTFE com 60% de bronze. A escolha do PTFE modificado para a substituição do PTFE convencional na formulação do compósito de PTFE com 60% de bronze deveu-se ao fato que polímero puro de PTFE modificado apresenta propriedades mecânicas e químicas superiores ao polímero puro de PTFE convencional, além de não apresentar limitações de disponibilidade, possibilitando a continuidade do crescimento dos segmentos industriais. A escolha do compósito de PTFE com 60% de bronze deveu-se ao fato que essa formulação é a mais empregada no segmento automobilístico para a fabricação de anéis para amortecedores e retentores. Após a substituição da resina de PTFE, os resultados demonstraram que o compósito de PTFE modificado com 60% de bronze apresentou propriedades inferiores ao compósito fabricado com PTFE convencional. A queda dessas propriedades pode estar relacionada com possíveis micros fissuras na estrutura do compósito em virtude de ar preso durante o processo de fabricação / Abstract: This work focuses on research studies of the properties of tensile strength and elongation of the composite of Polytetrafluoroethylene (PTFE) with 60% bronze after replacing the type of PTFE used in the formulation of this compound. Currently, this composite uses conventional PTFE in the formulation and the objective is to change to modified PTFE. The motivation for this change was due to the fact that the conventional PTFE has limited availability hindering the development of the segments that use the PTFE composite with 60% bronze. The choice of PTFE modified PTFE to replace the conventional formulation of the composite with 60% PTFE bronze was due to the fact that pure polymer modified PTFE has superior mechanical and chemical properties of the pure polymer PTFE conventional, and not present availability limitations, enabling the continued growth of industries. The choice of the composite with 60% PTFE bronze due to the fact that this formulation is the most used in the automotive sector for the manufacture of rings and seals for shock absorbers / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266830 |
| Date | 19 August 2018 |
| Creators | Bento, Ronaldo Euzébio |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Campos, João Sinézio de Carvalho, 1955-, Ribeiro, Alexandre Antunes, Mei, Lúcia Helena Innocentini |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 57 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0047 seconds