Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2013. / Made available in DSpace on 2013-07-16T21:07:25Z (GMT). No. of bitstreams: 1
316599.pdf: 2616486 bytes, checksum: 886fd2ef3956654c67a8a0360eae3bd7 (MD5) / Os materiais nanoestruturados (MN) FeSb2 e Sb2Te3 foram produzidos por moagem mecânica (MM) e tiveram suas propriedades estruturais e ópticas investigadas na condição de altas pressões, através de medidas in situ de padrões de difração de raios X (DRX) e espectros Raman (ER). As propriedades estruturais, térmicas e ópticas para a liga FeSb2 também foram estudadas nas condições ambiente, através de medidas de DRX, ER, calorimetria diferencial de varredura (DSC - Differential Scanning Calorimetry) e transmitância óptica (TO). Medidas in situ de DRX e ER em função da pressão foram realizadas para a liga FeSb2 para pressões até 28.2 e 45.2 GPa, respectivamente. As medidas de DRX revelaram que, com o aumento da pressão, ocorre degradação da fase ortorrômbica S.G Pnnm (fase I) estável em condições ambiente. Aumento de fração volumétrica de uma fase amorfa, nucleada durante o processo de MM é observado. A fração volumétrica da fase amorfa é máxima em 23.3 GPa. Entre 14.3 e 23.3 GPa uma fase tetragonal, com grupo espacial (S.G - space group) I4/mcm (fase II) é nucleada, porém até a máxima pressão aplicada, 28.2 GPa, não foi observada nenhuma transição total da fase I para a fase II através de medidas de DRX. Medidas de ER revelam que, para pressões acima de 21 GPa, o modo Raman ativo A1g referente a fase II começa a ser fracamente observado. Para maiores pressões, medidas de ER revelam uma transição da fase I para a fase II. Medidas de DRX e ER in situ em função da pressão foram realizadas para a liga Sb2Te3 para pressões até 19.2 e 25.5 GPa, respectivamente. As medidas DRX revelaram uma sequência de transições de fases: (1) A fase romboédrica (fase I), S.G R-3m, estável em condições ambientes, se transforma completamente em uma fase ortorrômbica (fase II), S.G C2/m, em torno de 13.2 GPa. (2) Entre 15.2 e 19.2 GPa, a fase II inicia uma transformação para uma terceira fase ortorrômbica (fase III), S.G C2/c. Em 19.2 GPa ainda há vestígios da fase II. Uma transição topológica eletrônica (ETT - electronic topological transition) foi observada através de medidas de DRX e ER em uma pressão em torno de 3.7 GPa.<br> / Abstract : Nanostructured materials (NM) FeSb2 e Sb2Te3 were produced by mechanical milling (MM). Their structural and optical properties were investigated under high pressure condition, via in situ measurements of patterns of X-ray diffraction patterns (XRD), and Raman spectra (RS). The structural, thermal and optical properties of FeSb2 were also studied of ambient conditions by XRD, RS, differential scanning calorimetry (DSC) and optical transmittance (OT). In situ XRD and RS measurements as a function of pressure were performed for the FeSb2 alloy for pressures up to 28.2 and 45.2 GPa, respectively. XRD measurements reveal that, with increasing pressure, degradation of the orthorhombic phase (phase I), S.G Pnnm, occurs. An increase in the volume fraction of an amorphous phase, nucleated during the MM process, is observed. The volume fraction of the amorphous phase is maximum at 23.3 GPa. Between 14.3 and 23.3 GPa a tetragonal phase, space group S.G I4/mcm (phase II) is nucleated, but until the maximum applied pressure, 28.2 GPa, the complete transition from phase I to phase II was not observed by XRD measurements. ER measurements show that for pressures above 21 GPa, the Raman active mode A1g, relative of phase II, begins to be faintly observed. For pressures higher than 21 GPa, measures of RS reveal a transition from phase I to phase II. XRD and RS measurements as a function of pressure were performed for the Sb2Te3 alloy for pressures up to 19.2 and 25.5 GPa, respectively. XRD measurements reveal a sequence of phase transitions: (1) the rhombohedra phase (phase I) with space group S.G R-3m, stable at ambient conditions, is completely transformed into a orthorhombic phase, S.G C2/m (phase II) around 13.2 GPa. (2) between 15.2 and 19.2 GPa, phase II begins a transformation to a third orthorhombic phase (phase III) with S.G C2/c. At 19.2 GPa there is still some remain of phase II. An electronic topological transition (ETT) was observed around 3.7 GPa.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/103525 |
| Date | January 2013 |
| Creators | Poffo, Claudio Michel |
| Contributors | Universidade Federal de Santa Catarina, Lima, João Cardoso de |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 134 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds