In this study, complex rolling technology is adopted to produce aluminum/copper clad metals . The aluminum alloy A1050 and the copper C1100 are used. The experimental plan : the roughness (RCu=3.5£gm¡ARAl=6.45£gm)¡A(RCu=1.0£gm¡ARAl =2.15£gm)¡A(RCu=0.35£gm¡ARAl=0.8£gm) the thickness ratio(tAl:tCu=3:1)¡A(tAl:tCu =2:2)¡A(tAl:tCu=1:3) reduction 60% and 70% are set. It shows that the influence of the thickness is more significant than the roughness on the curvature according to the experimental results. And the results of peeling tests show that the peeling strength for the reduction 70% is larger than that for 60%. And peel strength with the second time rolling is larger than that with only once. The average peeling strength of the specimen in the rolling direction is larger than that in the perpendicular direction.
From the micro Vickers hardness tests , it is known that the larger of the reduction of copper is, the larger the micro Vickers hardness between the interface of the sheets is .
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0903108-223805 |
Date | 03 September 2008 |
Creators | Lin, Hsu-wen |
Contributors | RAY-QUEN HSU, SU-HAI HSIANG, WEI-CHING YEH, YEONG-MAW HWANG, WOEI-SHYAN LEE |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | Cholon |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0903108-223805 |
Rights | campus_withheld, Copyright information available at source archive |
Page generated in 0.1422 seconds