Porous plates delivered calcium chloride at a negative potential to the top of blocks of partially welded (20.1 x 20.1 x 66.6 cm) and densely welded (30.1 x 20.1 x 48.1 cm) tuff with discrete fractures. During infiltration, flux increased through the partially welded block's fracture as the applied suction was lowered to 2.3 cm. The wetting front advanced 66.6 cm in 239 days. Chloride concentration and temporal moments from five tracer tests with 0 to 5 cm of applied suction indicated that preferential fracture flow occurred. Displacement transducer data reflect a decrease in fracture aperture at several months prior to but not during tracer tests. Fracture transmissivities decreased an order of magnitude (6.4 x 10⁻⁹ to 4.2 x 10⁻¹⁰ M²/s) as the applied suction increased from 0 to 5 cm while the tensiometer data indicated a suction of about 20 cm of water within the fracture and matrix. Highest during infiltration to an initially dry block, inflow losses of 3 to 44 percent due to evaporation are the greatest source of error for the constant potential method used.
| Identifer | oai:union.ndltd.org:arizona.edu/oai:arizona.openrepository.com:10150/277169 |
| Date | January 1989 |
| Creators | Myers, Kevin Christopher, 1965- |
| Contributors | Sully, Michael |
| Publisher | The University of Arizona. |
| Source Sets | University of Arizona |
| Language | en_US |
| Detected Language | English |
| Type | text, Thesis-Reproduction (electronic) |
| Rights | Copyright © is held by the author. Digital access to this material is made possible by the University Libraries, University of Arizona. Further transmission, reproduction or presentation (such as public display or performance) of protected items is prohibited except with permission of the author. |