The object of this thesis is to assess the structural stability of heterogeneous weld joint, which consists of two different base materials (16,537 steel and 16,236 steel) and weld metal NiCrMo2.5-IG with buttering layer P24-IG. All these materials belong to the group of low-alloyed creep-resistant steels that are to be used mainly in the power industry. The weld joint was made by application of the TIG hot wire welding method. Structural stability of this joint was evaluated by carbon redistribution and microstructural changes after annealing in temperature 300 °C and 400 °C during 500 hours. For modelling the phase composition of particular steels was used the ThermoCalc software. All gained results should be employed to appraise whether the heterogeneous weld joint of the steam turbine´s rotor is eligible for long-term operation in hard working conditions.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:230132 |
| Date | January 2012 |
| Creators | Jech, David |
| Contributors | Jan,, Vít, Foret, Rudolf |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0023 seconds