The thesis is focused on microstructural stability of heterogeneous weld joint of ODS steel and tungsten. The theoretical part summarizes the basic information about the structure and properties of ODS steels and describes the methods of joining these steels with tungsten. In the experimental part, materials MA956 and WL10 were welded by using electron beam. The individual samples differ by preheating temperature or use filler material. After annealing at 800 °C/1h and 1000 °C/5h, a change of the weld metal microstructure was evaluated by using scanning electron microscope. The chemical composition was measured by energy dispersive spectroscopy. It has been found that during annealing, massive precipitation of particles occures in the whole volume of the weld metal. These particles were identified as Laves phase.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:378410 |
| Date | January 2018 |
| Creators | Adam, Ondřej |
| Contributors | Sonnek, Pavel, Jan, Vít |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0013 seconds