Previous issue date: 2016-02-29 / Na união de materiais metálicos, sobretudo nos aços, os processos de soldagens
são predominantes e com grande destaque para soldas ao arco elétrico. E dentre os
processos de soldas ao arco elétrico há no segmento metal mecânico mundial uma
enorme utilização do GMAW que necessita de gases de proteção que evitam a
contaminação das áreas soldadas pelos gases presentes na atmosfera, em especial
o nitrogênio, o oxigênio e o hidrogênio. O GMAW por sua vez é subdividido em dois
tipos de processos de soldagens que dependem das características físicas e
químicas dos gases de proteção, bem como, do metal de base a ser soldado. O
primeiro deles quando se usa como gás de proteção um gás inerte como o argônio e
o hélio ou uma mistura de gases inertes sendo denominado então MIG. Já o
segundo tipo ocorre quando no gás de proteção há a presença de um gás ativo
como o oxigênio ou o dióxido de carbono ou uma mistura de gases ativos e inertes e
é conhecido como MAG. Foi realizada a coleta e a análise em Pernambuco dos
fumos (particulados) e gases gerados na soldagem GMAW, no soldador, em duas
empresas do segmento metal mecânico de Pernambuco de acordo com a NR-15 e a
ACGIH. A caracterização dos fumos foi obtida por ICP-OES enquanto, a dos gases
ocorreu por cromatografia em fase gasosa. O objetivo deste trabalho foi coletar e
analisar qualitativa e quantitativamente os fumos e os gases gerados no soldador no
processo de soldagem GMAW. E desenvolver uma metodologia eficiente e de baixo
custo na coleta e acondicionamento das amostras dos gases no soldador de duas
empresas do segmento metal mecânico de Pernambuco. A conclusão deste trabalho
se baseou nas análises dos fumos e dos gases, em cada um dos soldadores. E
indicou que nas duas empresas, cada soldador não estava exposto a fumos acima
dos limites da NR-15 e da ACGIH. As análises do CO2 e do CO, indicaram que o
soldador da empresa “A” não excedia os limites toleráveis da ACGIH e da NR-15. O
soldador da empresa “B” ficou exposto apenas ao CO acima do limite da ACGIH e
quanto ao CO2 não excedeu os limites da NR-15 e da ACGIH. / In the union of metallic materials, mainly in steel, welding processes are predominant
and with great emphasis on the electric arc welds. And among the processes of arc
welding to metal segment in the world there is a huge mechanical use of GMAW that
requires shielding gas to prevent contamination of the welded areas by gases
present in the atmosphere, in particular nitrogen, oxygen and hydrogen. The GMAW
is in turn subdivided into two types of welding processes that depend on the physical
and chemical characteristics of shielding gases, as well, as the base metal being
welded. The first of them when used as a shielding gas as an inert gas argon and
helium or a mixture of inert gases then being called MIG. The second type occurs
when there is the presence of an active gas such as oxygen or carbon dioxide or a
mixture of active and inert gas in the shielding gas and is known as MAG. Was
performed the collection and analysis in Pernambuco of the fumes (particulate) and
gases generated in GMAW welding, in the welder, in two companies of Pernambuco
mechanical metal segment of according to NR -15 and the ACGIH. The aim of this
work was to collect and analyze qualitatively and quantitatively the fumes and gases,
in the welder, in GMAW welding process. And develop an efficient methodology and
low cost in the collection and packaging of the samples of gases, in the welder, in the
GMAW welding in two metal mechanic segment companies Pernambuco. The
characterization of the smoke was obtained by ICP-OES while the gases occurred by
gas chromatography. The conclusion of this work was based on analysis of the
fumes and gases in each of the welders. And indicated that the two companies, each
welder was not exposed to fumes and gases or CO and CO2 above the limits of the
NR-15 and ACGIH. Analyses of CO2 and CO indicated that the welder of the
company "A" did not exceed the tolerable limits of the ACGIH and NR-15. Welder the
company "B" was exposed only to CO above the ACGIH limit and how much CO2
has exceeded the scope of the NR-15 and ACGIH.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/17933 |
Date | 29 February 2016 |
Creators | ALVES, Sérvulo José Ferreira |
Contributors | http://lattes.cnpq.br/6740759499723367, ARAUJO FILHO, Oscar Olimpio de |
Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Engenharia Mecanica, UFPE, Brasil |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0169 seconds