Orientadores: Mario Alexandre Coelho Sinhoreti, Carlos Jose Soares / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-11T16:18:48Z (GMT). No. of bitstreams: 1
Carlo_HugoLemes_D.pdf: 4484901 bytes, checksum: b6c246e6e05cdf7633210adfa7b73c84 (MD5)
Previous issue date: 2008 / Resumo: Baseado no entendimento incompleto de como o conteúdo de partículas de carga influencia nas propriedades mecânicas dos materiais de moldagem este estudo avaliou quantitativa e qualitativamente o conteúdo de partículas de carga inorgânicas presente em cinco marcas comerciais de alginatos (Jeltrate; Jeltrate Plus, Jeltrate Chromatic Ortho, Hydrogum e Ezact Krom) e nove marcas comerciais de siliconas de adição e/ou condensação nas consistências massa e/ou fluida (Clonage, Elite HD+ Light Body, Express Light Body, Flexitime, Optosil P Confort/Xantopren VL Plus, Oranwash L, Reprosil A+, Silon 2 APS e Virtual Extra Light Body). Foram realizados testes para determinar recuperação elástica e deformação sob compressão dos alginatos e dos elastômeros e estabelecer, dessa forma, uma correlação entre os resultados para partículas de carga e os testes mecânicos. O conteúdo volumétrico das partículas de carga foi determinado pesando-se as amostras submersas em água antes e após a queima das mesmas durante 3h a 450°C (alginatos) e a 600°C (siliconas). Quantidades determinadas de materiais não polimerizados foram lavadas em acetona e clorofórmio e recobertas com ouro para avaliação da morfologia e tamanho das partículas em M.E.V. A composição foi determinada por EDX. A recuperação elástica e a deformação sob compressão foram determinadas de acordo as especificações ? 1563 (alginatos) e 4823 (elastômeros) da ISO. O alginatos Jeltrate e Jeltrate Plus apresentaram os maiores valores médios para quantidade volumétrica de partículas de carga (%) enquanto o material Hydrogum apresentou os menores valores. A silicone de adição Flexitime Easy Putty apresentou os maiores valores de quantidade volumétrica de partículas, enquanto que a silicone de condensação Xantopren VL Plus apresentou os menores. As partículas de carga dos alginatos apresentaram-se, de forma geral, como objetos esféricos e com perfurações. O material Hydrogum apresentou forma de bastões cilíndricos e perfurados. As siliconas apresentaram morfologias variadas ¿ partículas trituradas, esféricas, esferóides, bastões cilíndricos perfurados e bastões misturados a partículas
usinadas. O alginato Ezact Krom apresentou os maiores valores médios de tamanho de partícula, enquanto que o alginato Hydrogum as menores. A silicone de condensação Clonage massa apresentou os maiores valores médios de tamanho de partícula, enquanto a silicone de adição Elite HD os menores. A análise da composição das partículas apresentou o silício como o elemento em maior quantidade. Com relação aos resultados de recuperação elástica, o alginato Ezact Krom e as siliconas Reprosil A+ massa e Flexitime fluida apresentaram os maiores valores de recuperação elástica, enquanto o alginato Jeltrate Plus e as siliconas Optosil P Confort e Clonage fluida apresentaram os menores. Os resultados de deformação sob compressão foram maiores para o alginato Jeltrate
Plus e para as siliconas Silon 2 APS massa e fluida. Os menores resultados foram apresentados pelo alginato Ezact Krom e as siliconas Reprosil A+ massa e Xantopren VL Plus. Todos os materiais estão em conformidade com a norma ISO ?1563, mas nem todos estão em relação à norma ?4823 / Abstract: Based on the incomplete understanding on how filler features influence the properties of elastomeric impression materials, the purpose of this study was to determine the inorganic filler fraction and size of five commercially available alginates (Jeltrate; Jeltrate Plus, Jeltrate Chromatic Ortho, Hydrogum e Ezact Krom) and nine addition/condensation silicones using the putty/light consistence (Clonage, Elite HD+ Light Body, Express Light Body, Flexitime, Optosil P Confort/Xantopren VL Plus, Oranwash L, Reprosil A+, Silon 2 APS e Virtual Extra Light Body). A SEM/EDX analysis was done to qualitatively characterize the materials. Soon afterwards elastic recovery and strain in compression of the alginates and some the silicones was carried. The inorganic particles volumetric fractions were accessed by weighing a previously determined mass of each material in water before and after burning samples for 3 hours at 450ºC (alginates) and 600ºC (silicones). Unsettled materials were soaked in acetone and chloroform and sputter-coated with gold for SEM evaluation of fillers¿ morphology and size. The filler composition was determined by EDX. Elastic recovery and strain in compression tests were conducted according to ISO specification number 1563 and 4823. Jeltrate and Jeltrate Plus presented the highest mean values of percentage content of inorganic particles in volume, while Jeltrate Chromatic Ortho presented the lowest values. Flexitime Easy Putty was the silicone with the highest mean value, while Xantopren VL Plus had the lowest value. The alginate fillers presented a circular appearance with helical form and various perforations. Hydrogum fillers looked like cylindrical, perforated sticks. SEM pictures of the silicone inorganic particles showed numerous morphologies ¿ lathe-cut, spherical, spherical-like, sticks, and sticks mixed to lathe-cut powder. Ezact Krom was the alginate with the highest values for diameter size, while Hydrogum had the lowest. Clonage Putty showed the highest values, while Elite HD+ Light Body presented the lowest
values. The component in higher concentration in the materials is silicon. The alginate Ezact Krom, and the addition cure silicones Reprosil A+ putty and Flexitime Correct Flow had the highest mean values of elastic recovery, while the alginate Jeltrate Plus and the condensation cured silicones Optosil P Confort and Clonage Putty presented the lowest values. Strain in compression test showed the alginate Jeltrate Plus and the condensation cured silicones Silon 2APS Putty and Fluid as the materials with the highest values. The alginate Ezact Krom and the silicones Reprosil A+ Putty and Xantopren VL Plus had lowest values. All materials are in conformity with the requirements of ISO specification number 1563, but not all materials are in conformity with the requirements of ISO specification number 4823 / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288141 |
| Date | 24 July 2008 |
| Creators | Carlo, Hugo Lemes |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Soares, Carlos José, Sinhoreti, Mário Alexandre Coelho, 1969-, Goiato, Marcelo Coellho, Gomes, Vanderlei Luiz, Correr Sobrinho, Lourenço, Leonardo, Rafael |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 84f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0033 seconds