Chemical vapor deposition of diamond thin films on titanium silicon carbide

Chemical vapor deposition (CVD) has been the main method for synthesizing diamond thin films on hetero substrate materials since 1980s. It has been well acknowledged that both nucleation and growth of diamond on non-diamond surfaces without pre-treatment are very difficult and slow. Furthermore, the weak adhesion between the diamond thin films and substrates has been a major problem for widespread application of diamond thin films. Up to now, Si has been the most frequently used substrate for the study of diamond thin films and various methods, including bias and diamond powder scratching, have been applied to enhance diamond nucleation density.
In the present study, nucleation and growth of diamond thin films on Ti3SiC2, a newly developed ceramic-metallic material, using Microwave Plasma Enhanced (MPE) and Hot-Filament (HF) CVD reactors were carried out. In addition, synchrotron-based Near Edge Extended X-Ray Absorption Fine Structure Spectroscopy (NEXAFS) was used to identify the electronic and chemical structures of various NCD films. The results from MPECVD showed that a much higher diamond nucleation density and a much higher film growth rate can be obtained on Ti3SiC2 compared with on Si. Consequently, nanocrystalline diamond (NCD) thin films were feasibly synthesized on Ti3SiC2 under the typical conditions for microcrystalline diamond film synthesis. Furthermore, the diamond films on Ti3SiC2 exhibited better adhesion than on Si. The early stage growth of diamond thin films on Ti3SiC2 by HFCVD indicated that a nanowhisker-like diamond-graphite composite layer, different from diamond nucleation on Si, initially formed on the surface of Ti3SiC2, which resulted in high diamond nucleation density. These results indicate that Ti3SiC2 has great potentials to be used both as substrates and interlayers on metals for diamond thin film deposition and application. This research may greatly expand the tribological application of both Ti3SiC2 and diamond thin films.
The results demonstrated that NEXAFS is a reliable and powerful tool to identify NCD films.

Identiferoai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:SSU.etd-09152009-072632
Date21 September 2009
CreatorsYang, Songlan
ContributorsYang, Qiaoqin, Zhang, Wenjun, Oguocha, Ikechukwuka N., Evitts, Richard W., Tsui, Ying Yin
PublisherUniversity of Saskatchewan
Source SetsLibrary and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada
LanguageEnglish
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://library.usask.ca/theses/available/etd-09152009-072632/
Rightsunrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report.

Page generated in 0.0018 seconds