Biopolymers from renewable resources are of interest for packaging applications as an alternative to conventional petroleum-based polymers. One of the major application areas for biopolymers is food packaging, where a candidate polymer should meet critical requirements such as mechanical and oxygen barrier performance, also in humid conditions. Starch has long been used in certain packaging applications, either in plasticized state or blended with other polymers. However, native starch has high sensitivity to water and low mechanical and barrier performance. Recently, wood-derived hemicelluloses have been extensively studied as oxygen barrier films, but suffer from low film-forming ability and mechanical performance. In the present study, xyloglucan (XG) from tamarind seed waste is explored as an alternative high-performance biopolymer in packaging applications. The obstacles of polysaccharides in terms of moisture sensitivity and processability are addressed in this thesis. In Paper I, film properties of XG were studied. XG has a cellulose backbone, but unlike cellulose, it is mostly soluble in water forming highly robust films. Moisture sorption isotherms, tensile tests and dynamic mechanical thermal analysis were performed. Enzymatic modification (partial removal of galactose in side chains of XG) was performed to study the effect of galactose on solubility and filmforming characteristics. XG films showed lower moisture sorption than starch. Stiffness and tensile strength were very high of the order of 4 GPa and 70 MPa respectively, with considerable ductility and toughness. The thermomechanical performance was very high with a softening temperature near 260 ºC. In Paper II, several plasticizers were studied in order to facilitate thermal processing of XG films: sorbitol, urea, glycerol and polyethylene oxide. Films of different compositions were prepared and studied for thermomechanical and tensile properties. Highly favorable characteristics were found with XG/sorbitol system. A large drop in glass transition temperature (Tg) of XG of the order of 100 ºC with 20 - 30 wt% sorbitol was observed with an attractive combination of increased toughness. In Paper III, XG was chemically modified and the structure-property relationship of modified XG studied. XG modification was performed using an approach involving periodate oxidation followed by reduction. The oxidation is highly regioselective, where the side chains of XG are mostly affected with the cellulose backbone well-preserved as noticed from MALDI-TOF-MS and carbohydrate analysis. Films were cast from water and characterized by dynamic mechanical thermal analysis, dynamic water vapor sorption, oxygen transmission analysis and tensile tests. Property changes were interpreted from structural changes. The regioselective modification results in new types of cellulose derivatives without the need for harmful solvents. In Paper IV, moisture durability of XG was addressed by dispersing montmorillonite (MTM) platelets in water suspension. Oriented bionanocomposite coatings with strong in-plane orientation of clay platelets were prepared. A continuous water-based processing approach was adopted in view of easy scaling up. The resulting nanocomposites were characterized by FE-SEM, TEM, and XRD. XG adsorption on MTM was measured by quartz crystal microbalance analysis. Mechanical and gas barrier properties were measured, also at high relative humidity. The reinforcement in mechanical properties and effects on barrier properties were remarkable, also in humid conditions. In Paper V, cross-linked XG/MTM composite was prepared with high clay content (ca. 45 vol%) by an industrially scalable “paper-making” method. Instead of using cross-linking molecules, cross-linking sites were created on the XG chain by selective oxidation of side chains. The in-plane orientation of MTM platelets were studied using XRD and FE-SEM. The mechanical properties and barrier performance were evaluated for the resulting 'nacre-mimetic' nanocomposites. The elastic modulus of cross-linked nanocomposites is as high as 30 GPa, one of the stiffest bionanocomposites reported. / <p>QC 20121107</p>
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-107043 |
Date | January 2012 |
Creators | Kochumalayil Jose, Joby |
Publisher | KTH, Biokompositer, KTH, VinnExcellens Centrum BiMaC Innovation, Stockholm |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Trita-CHE-Report, 1654-1081 ; 2012:53 |