Un-doped, Tb3+ as well as Yb3+ doped ZnO nanocrystals with different concentrations of RE3+ (Tb3+, Yb3+) ions were successfully synthesized via sol-gel method to produce rare earth activated zinc oxide nanophosphors. The phosphor powders were produced by drying the precursor gels at 200˚C in ambient air.
Based on the X-ray diffraction results, it was found that the pure and RE3+ doped ZnO nanophosphors were highly polycrystalline in nature regardless of the incorporation of Tb3+ or Yb3+ ions. Moreover, the diffraction patterns were all indexed to the ZnO Hexagonal wurtzite structure and belong to P63mc symmetry group. The Raman spectroscopy confirmed the wurtzitic structure of the prepared samples.
Elemental mapping conducted on the as prepared samples using Scanning electron microscope (SEM) equipped with energy dispersive X-ray spectrometer (EDX) revealed homogeneous distribution of Zn, O, and RE3+ ions. The high resolution transmission electron microscope (HR-TEM) analyses indicated that the un-doped and RE3+ doped samples were composed of hexagonal homogeneously dispersed particles of high crystallinity with an average size ranging from 4 to 7 nm in diameter, which was in agreement with X-ray diffraction (XRD) analyses.
ZnO:Tb3+ PL study showed that among different Tb3+ concentrations, 0.5 mol% Tb3+ doped ZnO nanoparticles showed clear emission from the dopant originating from the 4f-4f intra-ionic transitions of Tb3+ while the broad defects emission was dominating in the 0.15 and 1 mol% Tb3+doped ZnO. Optical band-gap was extrapolated from the Ultraviolet Visible spectroscopy (UV-Vis) absorption spectra using TAUC‟s method and the widening of the optical band-gap for the doped samples as compared to the un-doped sample was observed. The PL study of ZnO:Yb3+ samples was studied using a 325 nm He-Cd laser line. It was observed that the ZnO exciton peak was enhanced as Yb3+ions were incorporated in ZnO matrix. Furthermore, UV-VIS absorption spectroscopic study revealed the widening of the band-gap in Tb3+ doped ZnO and a narrowing in the case of Yb3+ doped ZnO system.
X-ray photoelectron spectroscopy demonstrated that the dopant was present in the doped samples and the result was found to be consistent with PL data from which an energy transfer was evidenced. Energy transfer mechanism was evidenced between RE3+ and ZnO nanocrystals and was discussed in detail. / Physics / M.Sc. (Physics)
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:unisa/oai:uir.unisa.ac.za:10500/14191 |
| Date | 11 1900 |
| Creators | Kabongo, Guy Leba |
| Contributors | Dhlamini, M.S., Mothudi, B.M. |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Dissertation |
| Format | 1 online resource (viii, 118 leaves) : illustrations (some color), color graphs, application/pdf |
Page generated in 0.0022 seconds