Syntéza, charakterizace a katalytické využití nových typů zeolitů / Synthesis, characterization and catalytic application of novel zeolites

The PhD thesis concerns the synthesis of novel zeolite materials, investigation of their properties and their possible use in catalytic application. The work was focused on the two- dimensional zeolites. The thesis was worked out at the Department of Synthesis and Catalysis at J. Heyrovský Institute of Physical Chemistry, AS CR. Germanosilicate UTL (Si/Ge molar ratio 4.0-6.5) was found to undergo unique structural changes in the neutral or acid environment leading to transformation of its three-dimensional framework into two-dimensional layered material denoted IPC-1P. The UTL degradation, so called top-down synthesis, was enabled due to a presence of double-four-units (D4Rs), which can be seen as supporting units/pillars between the rigid layers. The preferential location of Ge in D4Rs makes the units an ideal target for their selective degradation. The interlayer space in lamellar IPC-1P was modified by swelling with long-organic chain surfactant (material IPC-1SW). To keep the interlayer space permanently expanded (up to 3.3 nm) the silica amorphous pillars were subsequently introduced (material IPC-1PI). The integrity of the layers and their preserved UTL character was confirmed in all members of IPC-1 family by HRTEM and electron diffraction measuring. The layers of IPC-1P were condensed back...

Identiferoai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:338491
Date January 2014
CreatorsEliášová, Pavla
ContributorsČejka, Jiří, Štěpnička, Petr, Mintova, Svetlana
Source SetsCzech ETDs
LanguageEnglish
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/doctoralThesis
Rightsinfo:eu-repo/semantics/restrictedAccess

Page generated in 0.002 seconds