Avaliação do desempenho de filmes contendo silanos e sais de terras raras para proteção contra corrosão de camadas de ZnFe eletrodepositadas / Evaluation of the performance of films containing silanes and rare earth salts for protection of zinc-iron alloy electroplated against corrosion

Orientador: Celia Marina de Alvarenga Freire / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-13T07:27:48Z (GMT). No. of bitstreams: 1
Santos_MarciaCristinaGoncalvesdos_D.pdf: 5280662 bytes, checksum: 763649a5f0d49aa48853a896ab0335c2 (MD5)
Previous issue date: 2009 / Resumo: Aço galvanizado e aço eletrodepositado com liga ZnFe são materiais comuns na indústria de construção civil e automotiva. Esses materiais à base de zinco necessitam, entretanto, serem protegidos de ambientes corrosivos através de um tratamento de superfície que geralmente contém cromo hexavalente ( Cr6+), tóxico para o meio ambiente e cancerígeno para o homem. O presente trabalho apresenta um estudo com filmes contendo diferentes silanos: viniltrietoxissilano (VS), bis-(1,2-[trietoxissilil] etano) (BTSE) ou bis-(3-[trietoxissilil]-propil? tetrassulfeto (BTESPTS) e nitratos de terras raras (Ce ou La), como revestimentos de conversão para a camada de liga ZnFe. Esses sistemas foram avaliados através das análises de Espectroscopia Fotoelétrica de Emissão de Raios-X (XPS), das Curvas de Polarização, da Espectroscopia de Impedância Eletroquímica (EIE), da Microscopia Eletrônica de Varredura (MEV) e Espectrometria de Energia Dispersiva (EDS). Os resultados de EIE e polarização indicaram que os sistemas estudados foram eficientes contra corrosão e que seu desempenho dependia do tipo de silano. Os sistemas ZnFe+Ce+BTSE+BTESPTS e ZnFe+La+BTSE+BTESPTS mostraram o melhor resultado contra corrosão. / Abstract: Galvanized and zinc electroplated steels are very useful materials in automotive and construction industries. These zinc based materials, however, need to be protected against corrosive environments through a surface treatment that generally has hexavalent chromium wich is toxic to the environment and may cause cancer to human being. This thesis shows a study about films containing different silanes: vinyltriethoxysilane (VS), bis-(1,2-[triethoxysilyl]ethane) (BTSE) or is-(3-[triethoxysilyl]-propyl]tetrasulfide (BTESPTS) and rare earth nitrates (Ce, La) as conversion coatings to the zinc-iron alloy electroplated steel. These systems were evaluated using X-Ray Photoelectron Spectroscopy (XPS), Polarization Curves, Electrochemical Impedance Spectroscopy (EIS), Scanning Electron Microscopy (SEM) and EDS. The EIS and Polarization results have shown that the systems under study were efficient against corrosion and its performance depended upon the type of silane. The inciron+Ce+BTSE+ BTESPT and zinc-iron+La+BTSE+BTESPT systems have shown the best result against corrosion. / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263579
Date13 August 2018
CreatorsSantos, Marcia Cristina Gonçalves dos
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Freire, Celia Marina de Alvarenga, 1960-, Aoki, Idalina Vieira, Pessine, Elisabete Jorge, Duek, Eliana Aparecida de Rezende, Ierardi, Maria Clara Filippini
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format121 p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0022 seconds