This investigation was initiated by IBM to determine the types of cracks formed in hot-isostatic-pressed (HIP) Ni-Zn ferrite under impact and static loading conditions. A 1/8-inch tungsten carbide (WC) ball was used to apply the load in both cases. The impact loading condition was accomplished by dropping the WC ball from various heights between 40 and 200 cm. The static loading condition was accomplished by applying loads of 10 kg, 15 kg, and 30 kg on a Rockwell Hardness Tester. The response of HIP Ni-Zn ferrite to impact and static loading was elastic/plastic yielding permanent indentations. "Dimple" impressions, Hertzian-ring cracks, and radial cracks were formed upon applying increasing loads to the HIP Ni-Zn ferrite. As the grain size of the material was increased, both the Hertzian-ring and radial cracks were formed at lower loads compared to the as-received samples. The "dimple" impressions were not observed to follow this trend.
| Identifer | oai:union.ndltd.org:arizona.edu/oai:arizona.openrepository.com:10150/276523 |
| Date | January 1985 |
| Creators | Neumann, James, 1958- |
| Publisher | The University of Arizona. |
| Source Sets | University of Arizona |
| Language | en_US |
| Detected Language | English |
| Type | text, Thesis-Reproduction (electronic) |
| Rights | Copyright © is held by the author. Digital access to this material is made possible by the University Libraries, University of Arizona. Further transmission, reproduction or presentation (such as public display or performance) of protected items is prohibited except with permission of the author. |
Page generated in 0.0017 seconds