Superplasticity and creep behaviour in pure zirconia

An investigation of creep deformation in pure zirconia, using a creep-in-bending method with programmed temperature increase, showed the occurrence of superplasticity at temperatures near the monoclinic to tetragonal phase transformation. An interesting phenomenon was observed in a temporary halt to the creep process which occurred with continuing temperature increase beyond the phase transformation.
Temperature dependence tests at a maximum fibre stress of 3140 psi gave overall activation energies for the creep process in pure zirconia in the monoclinic and tetragonal phases of 44 and 103 kcal/mole respectively. / Applied Science, Faculty of / Materials Engineering, Department of / Graduate

Identiferoai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/36277
Date January 1967
CreatorsHart, John Laurie
PublisherUniversity of British Columbia
Source SetsUniversity of British Columbia
LanguageEnglish
Detected LanguageEnglish
TypeText, Thesis/Dissertation
RightsFor non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use.

Page generated in 0.0018 seconds