An investigation of the zirconium-rich corner of the zirconium-titanium-niobium constitutional diagram is described. X-ray techniques and metallography were used. A high-temperature x-ray goniometer attachment was employed to construct ternary isopleths. Isothermal sections and lattice parameter measurements are also outlined. The occurrence of a transitional ω -phase identified tentatively as tetragonal, is noted. The ternary constitutional data presented represent essentially a survey of the zirconium-rich corner and more detailed results must await further work. / Applied Science, Faculty of / Materials Engineering, Department of / Graduate
| Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/40137 |
| Date | January 1958 |
| Creators | Whitmore, Bruce Cecil |
| Publisher | University of British Columbia |
| Source Sets | University of British Columbia |
| Language | English |
| Detected Language | English |
| Type | Text, Thesis/Dissertation |
| Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0229 seconds