The swelling mechanisms of U3Si2 under neutron irradiation in reactor conditions are not unequivocally known. The limited experimental evidence that is available suggests that the main driver of the swelling in this material would be fission gases accumulation at crystalline grain boundaries. The steps that lead to the accumulation of fission gases at these locations are multiple and complex. However, gradually, the gaseous fission products migrate by diffusion. Upon reaching a grain boundary, which acts as a trap, the gaseous fission products start to accumulate, thus leading to formation of bubbles and hence to swelling. Therefore, a quantitative model of swelling requires the incorporation of phenomena that increase the presence of grain boundaries and decrease grain sizes, thus creating sites for bubble formation and growth. It is assumed that grain boundary formation results from the conversion of stored energy from accumulated dislocations into energy for the formation of new grain boundaries.This thesis attempts to develop a quantitative model for grain subdivision in U3Si2 based on the above mentioned phenomena to verify the presence of this mechanism and to use in conjunction with swelling codes to evaluate the total swelling of the pellet in the reactor during its lifetime.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/53970 |
| Date | 21 September 2015 |
| Creators | Marquez, Matias G. |
| Contributors | Petrovic, Bojan, Ougouag, Abderrafi |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Language | en_US |
| Detected Language | English |
| Type | Thesis |
| Format | application/pdf |
Page generated in 0.0023 seconds