Orientador: Rafael Leonardo Xediek Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T01:07:44Z (GMT). No. of bitstreams: 1
Cardoso_Leandro_M.pdf: 718836 bytes, checksum: 03cc173acd1c7745a9df4dd35a8a70dc (MD5)
Previous issue date: 2009 / Resumo: O objetivo deste trabalho foi verificar a resistência ao impacto da união denteresina acrílica, sob efeito da desinfecção simulada por energia de microondas. Cento e sessenta matrizes retangulares de cera utilidade (30x15x5mm) foram incluídas na parte inferior de muflas, com gesso pedra tipo III. Depois da cristalização do gesso, a cera foi removida e cada um dos 160 moldes de gesso resultante foi preenchido com silicone laboratorial. Sobre o silicone foi adaptado um dente molar de resina acrílica contendo um cilindro de cera (25mm de comprimento por 6mm de diâmetro) fixado na base. O conjunto foi revestido com silicone, a mufla preenchida com gesso pedra tipo III e levada à prensa de bancada por 1 hora. Em seguida, a mufla foi aberta e os conjuntos dente-cilindros removidos dos moldes. Os dentes foram escovados com solução de água quente e detergente líquido e adaptados nos moldes, com as bases submetidas previamente aos seguintes tratamentos: 1- sem tratamento, 2- desgaste com broca, 3- retenção com broca e 4- condicionamento com monômero. Oitenta cilindros de resina unidos à base dos dentes foram confeccionados com resina acrílica Clássico, em ciclo de água à temperatura de 74ºC por 9 horas, em termopolimerizadora automática (Termotron) e outros 80 com resina para microondas Onda-Cryl, em forno doméstico com 900W de potência: fase 1- três minutos com 40% da potência; fase 2- quatro minutos com 0% da potência; e fase 3- três minutos com 90% da potência. Os corpos-de-prova foram desincluídos após esfriamento das muflas em bancada. Metade dos corpos-de-prova de cada resina foi submetido à desinfecção simulada por microondas, em forno doméstico a 650W por 3 minutos, imersos individualmente em 150mL de água. Os demais corpos-de-prova não foram desinfectados (controle). Após armazenagem em água à temperatura de 37ºC por 24 horas, os corpos-de-prova foram submetidos ao teste de resistência ao impacto da união dente-resina, numa máquina Otto Wolpert Werke (sistema Charpy) com 40 kpcm de impacto. Os resultados obtidos foram submetidos à análise de variância e ao teste de Tukey para comparação das médias, em nível de 5% de significância. Os diferentes tratamentos na base dos dentes promoveram diferentes efeitos sobre a resistência da união dente-resina, em ambas as condições de desinfeção por microondas / Abstract: The aim of this study was to evaluate the effect of microwave disinfection in bond strength of acrylic teeth and a denture base resin. A hundred sixty rectangular wax patterns (30x15x5mm) were embedded in flasks with type III dental stone. After cristalization, the resulting moulds were filled with laboratorial silicone (Zetalabor), in which a molar acrylic tooth was included (36 Biotone IPN Vita) using a cylindrical wax (6x25mm) to join to the tooth base. The set was invested using laboratorial silicone and type III dental stone. After 1 hour, the flask was opened, the cylindrical wax removed from the tooth. Teeth were adapted in the moulds with the ridge laps submitted previously to the following treatments: 1 - no treatment; 2 -bur abrasion; 3 - bur grooving, and 4 - etched by monomer. Eighty rods of the Clássico acrylic resin atached to the tooth ridge lap were polymerized in bath cycle at 74ºC for 9 hours and deflasked after flask cooling, and 80 of Onda-Cryl acrylic resin were polymerized in 900W-domestic microwave oven following manufacturer's instructions. Specimens were deflasked after bench cooling. Fourty specimens of each acrylic resin were submitted to microwave disinfection, in a domestic oven at 650W for 3 minutes, individually immersed in 150mL of water. Other specimens were not disinfected (control). Specimens were stored in water at 37oC for 24 hours before impact test. Charpy impact strength test was performed using an impact testing machine (Otto Wolpert Werke) calibrated to 40 kpcm. Data were submitted to analysis of variance and Tukey's test at 5% of significance level. Different treatments on tooth ridge lap promoted different effects in the tooth-resin bond strength, in both conditions of simulated disinfection by microwave energy / Mestrado / Protese Dental / Mestre em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288555 |
Date | 13 August 2018 |
Creators | Cardoso, Leandro |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Rafael Leonardo Xediek, 1974-, Lopes, Murilo Baena, Henriques, Guilherme Elias Pessanha |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 40 f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |