Uniform and aligned nanofibers have been obtained by eletrospinning. Activated carbon nanofibers (ACNFs) have been used as electrode materials for battery and electric double layer due to its porous properties. A high value of surface area can be attained (1000 - 3000 nm) by activation, due to the presence of micropores on the surface of nanofibers.
A series of nanofibers have been prepared using different polymer precursors and concentrations by electrospinning in this study. Morphological study by SEM reveals a uniform and aligned fibrous structure for the PAN-based CNF (11 wt%) and a curved and twisted fibrous structure for the PAN-based CNF (8 wt%) and the acrylic-based CNF (9 wt%). Thus, the microstructure of CNF can be greatly influenced by the concentration of polymer precursor; high quality of nanofibers can be produced with higher polymer concentration and higher viscosity. The diameter of PAN-based nanofibers is gradually decreased from 400 to 200 nm during stabilization, carbonization, and activation, due mainly to the degradation and condensation. Surface of CNF becomes rough after activation due to the etching by potassium ions at high temperatures. Microstructural study by X-ray diffraction and Raman spectroscopy indicates a discernible diffraction peak at d002 = 0.356 nm and the ratio ID/IG = 1.83 of ACNFs, showing an amorphous and disordered structure, and leading to a low conductivity. Adsorption/desorption isotherms obtained from BET measurements under nitrogen atmosphere suggests a relatively small surface area of 8-10 m2/g, indicating that there might be no adsorption on the porous ACNF or the porous structure has been destroyed after carbonization. This leads to a relatively low conductance of 17 Faraday/g measured from the cyclic voltammetry.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0727112-165257 |
| Date | 27 July 2012 |
| Creators | Wu, Kuan-chung |
| Contributors | Bing-Hwai Hwang, Kuo-Kuang Cheng, Tzu-Chien Hsu |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0727112-165257 |
| Rights | unrestricted, Copyright information available at source archive |
Page generated in 0.002 seconds