This Master’s thesis deals with the problematics of radically initiated compounding of polyethylene by 1-vinyladamantane. Theoretical part focuses on the theory of grafting processes and how they are influenced by chosen process parameters, as well as the properties of used monomer. In experimental part, two sets of experiments were designed, in both cases the chemicals used were polyethylene LITEN MB 87, (2,5-dimethyl-2,5-bis(tert-butylperoxy) hexane), also called Trigonox 101, as the initiator, and chemicals called Ionol and Irgafos 168 as stabilizers. The experiments were carried out in a Brabender batch mixer, the temperature was 180 – 185 °C, the reaction time was 5 minutes. The analytic methods used to evaluate the prepared samples’ properties were the tensile testing, the Charpy notch test, measuring of the melt flow index, analyzing the torque during kneading and the analysis of infrared spectra of the samples. By carrying out of these experiments it was found that excessive crosslinking was present with mass fraction of initiator being as low as 2 %. It was also concluded that under these conditions the modification does not improve tensile properties of the material, but it does improve the impact strength, albeit slightly. The influence of the modification on flow properties needs to be investigated further. A presence of vinyl groups was observed in infrared spectra, suggesting the presence of ungrafted vinyladamantane.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:438897 |
| Date | January 2018 |
| Creators | Horkel, Ondřej |
| Contributors | Kučera, Jaroslav, Petrůj, Jaroslav |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds