Orientador: Wolney Luiz Stolf / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-13T23:25:07Z (GMT). No. of bitstreams: 1
Fajardo_RenatoSalviato_M.pdf: 6551186 bytes, checksum: dfafba047cc25e1cf74a6d2d2a1f50a3 (MD5)
Previous issue date: 1991 / Resumo: Devido a grande controvérsia em torno da adaptação de coroas cimentadas, decidimos analisar a efetividade na sua retenção quando consideradas justas, com pequeno espaço e aliviadas, quando eram fixadas.em preparos feitos em molares humanos (in vitro) com os seguintes meios de cimentação: - Fosfato de zinco na consistência obtida pelo teste de consistência da esp. n. 28 da A.D.A.; - Fosfato de zinco em consistência fluida; - Policarboxilato de zinco em proporção preconizada pela fabricante; - Policarboxilato de zinco em consistência fluida; - Resina fluida sem carga (tipo BIS-GMA). Estes conjuntos foram estudados tanto em linha de cimentação quanto em resistência à remoção das coroas através de ensaios tracionais. Submetendo os resultados obtidos a avaliação estatística, ficou evidenciado quê: - O meio resina obteve, em todas as condições de adaptação de coroa, linha de cimentação não detectável, pelo método adotado, e na condição coroa justa, proporcionou resultados de retensão semelhantes estatisticamente a todos os outros meios. - No geral, o meio cimentante fosfato de zinco normal foi o que proporcionou maior resistência à remoção de coroas, enquanto a resina foi o que proporcionou a menor resistência. -As coroas em condição de adaptação justa proporcionaram
os melhores resultados de retenção seguidas das intermediárias e depois as aliviadas. - No geral, somente o meio resina apresentou diferença
estatística quanto a linha de cimentação mostrando-se a mais eficaz no assentamento de coroas / Abstract: Due to the big controversy about fixed crown adaptation, we have decided to analyse the retention effectiveness when they were made tightly, with a small space and reliefed, and cemented on human molars with following cementation mediums: - Zinc Phosphate in consistency obteined by the n. 8 esp. consistency test of A.D.A. - Zinc Phosphate in fluid consistency. - Zinc Policarboxilate in proportion recomended by the
manufaturer. -Zinc Policarboxilate in fluid consistency. - Fluid Resin without fill-type BIS-GMA. These samples were studied as far as the film thickness,
as well as the crown retention resistance to tensional tests. According to the statistic avaliation, we can conclude that: - The Resin had no detectable interference in any adaptation condition and in the tight adaptation, it was statistically similar to the other products. -The Zinc Phosphate, in normal consistency, permited the highest retention resistance, while the Resin produced the least. - The crowns in tight adaptation had the best results in
retention followed by the ones with small space and reliefed. - Only the Resin showed statistic differences in film thickness beeing the best in the crown fitting / Mestrado / Materiais Dentarios / Mestre em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290273 |
| Date | 05 February 1991 |
| Creators | Fajardo, Renato Salviato |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Stolf, Wolney Luiz, 1937- |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Ciências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 102f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds