Programa de Pós Graduação em Engenharia Civil. Departamento de Engenharia Civil, Escola de Minas, Universidade Federal de Ouro Preto. / Submitted by giuliana silveira (giulianagphoto@gmail.com) on 2016-03-22T17:37:44Z
No. of bitstreams: 1
DISSERTAÇÃO_ViabilidadeTécnicaUso.pdf: 14392848 bytes, checksum: 7d274b3f0339684d0c74ca020c38d8fc (MD5) / Approved for entry into archive by Oliveira Flávia (flavia@sisbin.ufop.br) on 2016-04-15T13:08:58Z (GMT) No. of bitstreams: 1
DISSERTAÇÃO_ViabilidadeTécnicaUso.pdf: 14392848 bytes, checksum: 7d274b3f0339684d0c74ca020c38d8fc (MD5) / Made available in DSpace on 2016-04-15T13:46:43Z (GMT). No. of bitstreams: 1
DISSERTAÇÃO_ViabilidadeTécnicaUso.pdf: 14392848 bytes, checksum: 7d274b3f0339684d0c74ca020c38d8fc (MD5)
Previous issue date: 2016 / Os aditivos são produtos químicos adicionados ao concreto ou argamassa para
melhorar suas características no estado fresco ou endurecido. Comercialmente, existem mais
de 20 tipos de aditivos, sendo um deles os aditivos incorporadores de ar (AIA). Os AIA
promovem a formação de microbolhas de ar na pasta de cimento, melhorando a
trabalhabilidade e a coesão das matrizes cimentícias, além da sua resistência à ciclos de
congelamento. O princípio ativo destes aditivos são substâncias surfactantes, bem como o
de detergentes lava-louças. O detergente doméstico é um produto de ampla disponibilidade,
fácil aplicação, atóxico, relativo baixo custo e menor impacto ambiental, visto que são
substâncias biodegradáveis, por regulamentação. Assim, o presente trabalho propõe o uso
de um surfactante biodegradável presente em detergentes lava-louças, Linear Alquil
Benzeno Sulfonato de Sódio (LAS), como agente incorporador de ar sustentável para
matrizes de concreto e argamassa. Neste trabalho é feita uma avaliação de desempenho do
AIA proposto, comparando os resultados de matrizes de argamassa com a dosagem obtida
do AIA proposto com AIA comerciais e matrizes sem aditivos. A metodologia utilizada para
determinação do desempenho fundamenta-se em análises mecânicas das matrizes
produzidas, de sua microestrutura e demais propriedades de interesse para compostos de
cimento Portland em seu estado fresco e endurecido, conforme normalização ABNT. Notase
que, com o aumento da concentração de surfactantes, tem-se aumento do teor de ar
incorporado da matriz, melhoria na sua trabalhabilidade, redução na sua massa específica e
nos picos de temperatura na hidratação do cimento. Por outro lado, houve queda nas
propriedades mecânicas e um ligeiro retardo no tempo de fim de pega. Cabe notar que o AIA
proposto mostrou-se mais eficiente do que o AIA comercial em relação ao volume de ar
incorporado e à estabilidade do sistema de poros formado. A partir da caracterização
mecânica e física, foi possível determinar a eficácia do AIA proposto, bem como sua faixa
de dosagem ótima. Foi possível também associar a microestrutura das matrizes resultante
com suas propriedades mecânicas e físicas. Busca-se, assim, contribuir com o
desenvolvimento tecnológico das matrizes cimentícias no Brasil e no mundo. __________________________________________________________________________ / ABSTRACT : Chemical admixtures are products added to concrete or mortars in order to improve
their properties on the fresh and/or hardened state. Commercially, there are over 20 types of
chemical admixtures, such as the Air Entraining Admixtures (AEA). The AEA promote the
formation of microbubbles in the cement paste, improving the workability and cohesion of
cement-based composites, besides their resistance to freeze-thaw cycles. The active principle
of these admixtures are surfactants, analogously to washing up liquids. Washing up liquids
(or dishwashing liquids) are widely available products, relatively inexpensive and presenting
small environmental impact, since they are biodegradable substances, by regulation.
Therefore, the present work proposes the use of a biodegradable surfactant comprised in
washing up liquids, Linear Alkylbenzene Sulfonate (LAS), as sustainable air entraining
agent for mortar and concrete. In this sense, a performance evaluation of the proposed AEA
is carried out, by comparing the properties of mortars with proposed AEA, commercial AEA
and ones without any admixture. The methodology for performance evaluation is based on
physical, mechanical and microstructural analysis of the cement-based composites, in their
fresh and hardened state, according to Brazilian Standards, ANBT. Results show that, with
increasing concentration of surfactants on the mortar matrices, the air entrained content
increases, the workability is improved, and there is a reduction on the specific gravity, along
with their cement hydration temperature peaks. On the other hand, a decrease on mechanical
properties was observed, in addition to a delay on setting time. It is worth noticing that the
proposed AEA proved to be more competent than the commercial AEA regarding air
entrained volume and stability of the pore system. From the physical and mechanical
characterization, it was possible to determine the efficiency of the proposed AEA, as well as
its optimum range of dosage. It was also possible to associate the microstructure of the
mortar matrices with their physical and mechanical properties. As a result, we seek to
contribute to the technical development of cement-based composites in Brazil and in the
world.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:123456789/6409 |
| Date | January 2016 |
| Creators | Mendes, Júlia Castro |
| Contributors | Peixoto, Ricardo André Fiorotti |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFOP, instname:Universidade Federal de Ouro Preto, instacron:UFOP |
| Rights | Autorização concedida ao Repositório Institucional da UFOP pelo autor, 04/03/2016, com as seguintes condições: disponível sob Licença Creative Commons 4.0, que permite copiar, distribuir e transmitir o trabalho, desde que seja citado o autor e licenciante. Não permite o uso para fins comerciais nem a adaptação desta., info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds