This thesis deals with development of shrinkage reducing admixtures designed for alkali activated materials based on blast furnace slag. The main task of this work is to select the most suitable shrinkage reducing admixture based on experiments, in which can be observed minimal shrinkage and at the same time it will not adversely affect the properties of alkali activated blast furnace slag. In the experimental part of the work, test beams containing shrinkage reducing admixtures were prepared, in which the shrinkage and loss of weight were measured. Moreover, the mechanical properties of individual beams, such as tensile strength and compressive strength, were measured. Next, the surface tension of individual shrinkage reducing admixtures was measured in a mixture with pore solution. The hydration process of alkali activated materials under the action of reducing shrinkage admixtures was monitored by calorimetric analysis. The microstructure of the prepared samples was observed by scanning electron microscopy.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:376885 |
| Date | January 2018 |
| Creators | Šístková, Pavlína |
| Contributors | Bílek, Vlastimil, Kalina, Lukáš |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds