Alkali activated materials (AAMs) represent construction materials with a huge potential especially because of environmental and economic aspects but sufficient mechanical properties as well. A fibre or fabric reinforcement of the AAMs could support more widespread application potential due to the mechanical properties, fracture toughness or composite durability improvement. Various alkaline activators were used for a blast furnace slag (BFS) activation to produce a suitable matrix for basalt fibres (BF) implementation in this thesis. The BFs represent applicable reinforcing material because of its favourable mechanical and thermal properties. Still, the utilization of BFs in the AAMs is quite limited due to the fibres low chemical stability under the alkaline conditions. Accelerated leaching tests with a determination of basalt fibres chemical composition same as tensile strength change using various analytical techniques (XRD, XPS, SEM-EDX, ICP-OES) have confirmed these assumptions. An influence of basalt fabric reinforcement in one or more layers on the mechanical properties was determined with the meaning of the compressive and flexural strengths. The fibre/matrix adhesion and transition zone properties were studied using SEM-EDX and pull-out tests as well because they are crucial parameters for the composite material reinforcement efficiency.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:377316 |
| Date | January 2018 |
| Creators | Hrubý, Petr |
| Contributors | Šoukal, František, Kalina, Lukáš |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0016 seconds