Dealloying refers to the partial, selective dissolution of the less noble component(s) of a binary or ternary alloy precursor, resulting in a noble-rich, porous structure that has high surface area. Such surface structure is beneficial for fuel cells (FC) because FC uses platinum (Pt), a scarce metal, to catalyze the oxygen reduction reaction (ORR) at the cathode surface. In order to characterize the benefit of the dealloying process in FC ORR catalysts with the rotating disk electrode (RDE) technique, a high surface area catalyst support, namely 3M Co’s nanostructured thin film (NSTF), was incorporated into the RDE measurements. NSTF-coated glassy carbon (GC) disks were used in RDE experiments on a Pt/Pt1-xIrx (0.05 < x < 0.3) composition spread. ORR measurements using NSTF-coated GC disks measure the catalytic properties with the same morphology, composition and surface structure as would be found in a fuel cell. A series of Pt1-xCox and Pt1-xNix (0.5 < x < 0.8) dealloy catalyst precursor films were tested using NSTF-coated GC disks in RDE studies. The value of x in Pt1-xMx (M = Ni, Co) was selected to be high in order to examine the dealloying process. The catalyst films were examined by a RDE test protocol that tracked the surface enhancement factor (SEF) and ORR current densities over a large number of test cycles. The aim was to measure the catalytic performance of the Pt-M materials as dealloying took place. The SEF of the PtCo and PtNi materials increased rapidly at the beginning and reached a plateau as high as 50 cm2/cm2 while the specific ORR activities increased as the initial M content in the catalyst precursor increased. The impact of the dealloying process on morphology was examined by completely dealloying a Pt3Ni7 precursor, deposited on mirror-polished GC disks, at a constant potential. As the dealloying process continued, the SEF of the material increased from about 1 cm2/cm2 to > 30 cm2/cm2 and resulted in the formation of whisker-like structures.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:NSHD.ca#10222/14247 |
| Date | 22 August 2011 |
| Creators | Liu, Gary Chih-Kang |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | English |
| Detected Language | English |
Page generated in 0.0022 seconds