Binary alloys of manganese and boron and ternary alloys of manganese and boron with aluminum, zinc, tin and indium were prepared. Their structures were determined from x-ray powder photographs, and their ferromagnetic properties were measured with a Sucksmith rinf balance, using a powerful electromagnet. The orthorhombic phase MnB had a ferromagnetic Bohr magneton number of 1.73 per molecule and a Curie point of 309°C. Most of the ternary alloys were slightly ferromagnetic, but no strongly ferromagnetic single phase regions were found.
Paramagnetic measurements on Heusler alloys showed that they followed the Curie-Weiss law for the restricted range of temperature in which measurements could be made. / Applied Science, Faculty of / Materials Engineering, Department of / Graduate
| Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/41132 |
| Date | January 1954 |
| Creators | Swanson, Max Lynn |
| Publisher | University of British Columbia |
| Source Sets | University of British Columbia |
| Language | English |
| Detected Language | English |
| Type | Text, Thesis/Dissertation |
| Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0023 seconds