M. Tech. Metallurgical Engineering / Titanium and its alloys exhibit poor tribological characteristics. The poor resistance to sliding wear of Ti6Al4V alloy makes it susceptible to severe wear at the surface during sliding contact. This could cause galling and seizing during sliding contact. Ti6Al4V alloy also have poor corrosion resistance under critical conditions. Some problems with Ti6Al4V MMCs produced by laser cladding technique in most cases is poor bonding as a result of wetting properties between the ceramic and metal powders for reinforcement. Occurrence of porosity is another factor which can reduce the mechanical properties of MMCs. Occurrence of agglomerates is also a concern due to poor mixing of reinforcement powders. This project is aimed at investigating the effect of laser cladding of titanium alloy substrate with zirconium (Zr), titanium carbide (TiC), titanium (Ti) reinforcement additions. The effect of combination of these powders using various fractions and variable cladding parameters on the substrate will be investigated.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:tut/oai:encore.tut.ac.za:d1000737 |
| Date | January 2013 |
| Creators | Ochonogor, Onyeka Franklin |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Text |
| Format |
Page generated in 0.002 seconds