Tecnica de nanorisco para analise de adesão de revestimento de HA, depositada atraves de aspersão por plasma, sobre liga de titanio / Nanoscratch test applied to adhesion analysis of HA coated by plasma spray process over titanium alloy

Orientador: Cecilia A. C. Zavaglia / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-25T02:10:22Z (GMT). No. of bitstreams: 1
Fernandes_BeatrizLuci_D.pdf: 8612737 bytes, checksum: 5b82e95884b98b376d5146b5ea2586e9 (MD5)
Previous issue date: 1999 / Resumo: Apesar dos 30 anos de história, engenheiros e pesquisadores continuam procurando soluções para problemas que persistem até os dias de hoje, em relação à resistência ao desgaste de superfícies articuladas e à fixação aos tecidos ósseos de implantes ortopédicos de quadril. Esses problemas estão interligados, desde que a formação de grandes partículas nas articulações é o principal fator responsável pela perda da prótese e a qualidade da fixação do implante determina a produção dessas partículas. O material das amostras, analisadas neste trabalho, foi um dos empregados atualmente em próteses totais de quadril não cimentadas, ou seja, liga Ti6Al-7Nb revestida de hidroxiapatita (HA), aplicada através da técnica de aspersão por plasma. O principal objetivo deste trabalho foi apresentar uma alternativa para a avaliação da resistência da interface, utilizando-se uma nova técnica, rápida e confiável. As informações contidas estão relacionadas à técnica de deposição de materiais em forma de pó através de aspersão por plasma; ao estudo da resistência à adesão da HA sobre a liga de titânio através de ensaio de nanorisco e à caracterização superficial das amostras por determinação da rugosidade superficial, difração de raio-X e imagens do Microscópio Eletrônico de Varredura / Abstract: In spite of 30 years of history, engineers and researchers in general, are still trying to find solutions for the problems related to wear resistance of sliding surfaces and related to biological attachment of hip prostheses. These two questions are connected since the debris released in the joints are the main factor for loosing the prostheses and the fixation quality determines the production of those debris. The samples analyzed on this work were made of materials presently applied on hip prostheses like Ti-6Al-7Nb alloy with hydroxyapatite coating applied by plasma spray method. The main purpose of this work was to present an alternative to analyze the adhesion strength between the HA and the Ti-6Al-7Nb alloy using a new technique, fast and reliable. The information presented are related to the plasma spray' s deposition technique using powdered materials, to the evaluation of the interface between the two materials through the nanoscratch test and to the surface characterization using a mechanical profiler (profilometer), an X-Ray Diffract meter and a Scanning Electron Microscope / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263416
Date29 July 1999
CreatorsFernandes, Beatriz Luci
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Zavaglia, Cecília Amélia de Carvalho, 1954-, Zavaglia, Cecilia A. C., Conceição, Ideonor Novaes da, Carrera, Luiz Carlos Marques, Junior, Rubens Caram, Zoqui, Eugênio José
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format106p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0024 seconds