Avaliação das propriedades mecânicas e metalúrgicas de juntas soldadas pelo processo de fricção com pino consumível, em aço estrutural de alta resistência classificado como grau R4 pela norma IAC W22

Este estudo tem por objetivo avaliar a possibilidade de confeccionar juntas soldadas pelo processo de soldagem por fricção com pino consumível (Friction Hydro Pillar Processing), em aço classificado como grau R4 de acordo com a norma IAC W22. As juntas soldadas foram produzidas com três diferentes forças axiais: 30 kN, 45 kN e 60 kN, e após a soldagem, submetidos a três diferentes tempos de tratamento térmico de revenimento: uma hora, duas horas e quatro horas, na temperatura de 650 C. A microestrutura predominantemente martensítica resultante destes processos, foi caracterizada através de microscopia óptica, e de um mapeamento de microdureza Vickers. As soldas tiveram suas zonas afetadas pelo processo mensuradas através do software de análise de imagens ImageJ, sendo observadas maiores zonas para menores forças axiais empregadas. Caracterizou-se ainda, o nível de tensões residuais oriundos do processo de soldagem através do método de difração de nêutrons, para uma solda produzida com força axial de 45 kN, em duas diferentes condições, no estado de como soldado e com revenimento de quatro horas após a soldagem. Com os resultados obtidos neste trabalho pode-se concluir que as juntas soldadas com a força de 60 kN apresentaram a melhor combinação de propriedades avaliadas, que são, um menor tamanho de zonas afetadas pelo processo, e manteve um bom nível de dureza mesmo após o revenimento. Todas as juntas soldadas apresentaram uma ótima união metalúrgica, e os diferentes tempos de tratamento térmico empregados promoveram alterações microestruturais e nas propriedades do material já esperadas para o tratamento térmico de revenimento. / The aim of this study is to evaluate the possibility of making joints welded by Friction Hydro Pillar Processing, in steel grade R4 according to IAC W22. The repairs were produced with three different axial forces: 30 kN, 45 kN and 60 kN, and after welding, subjected to three different tempering heat treatment times: one hour, two hours and four hours, at a temperature of 650 C. The predominantly martensitic microstructure resulting from these processes was characterized by optical microscopy and a Vickers microhardness mapping. The welds had their zones affected by the process measured through the ImageJ image analysis software, with larger zones being observed for smaller axial forces employed. It was also characterized the level of residual stresses from the welding process, through the neutron diffraction method, for a weld produced with axial force of 45 kN, in two different conditions, as welded and annealing for four hours after welding. With the results obtained in this work it can be concluded that the welded joints with the force of 60 kN presented the best combination of evaluated properties, which are, a smaller size of zones affected by the process, and maintained a good level of hardness even after the annealing. All the welded joints presented an excellent metallurgical bonding, and the different times of thermal treatment employed promoted microstructural changes and in the properties of the material already expected for the heat treatment of annealing.

Identiferoai:union.ndltd.org:IBICT/oai:www.lume.ufrgs.br:10183/170297
Date January 2017
CreatorsMagalhães, Márcio Medeiros de
ContributorsReguly, Afonso
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UFRGS, instname:Universidade Federal do Rio Grande do Sul, instacron:UFRGS
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0019 seconds