The subject of this thesis are the rheological properties of cement paste with the addition of amorphous silicon dioxide. The basic rheological parameters are that describe the behavior of cement pastes in the fresh state. The work also included rheological tests including measurement principle and method of evaluation. Effect of mineral admixtures with high content of amorphous SiO2 is summarized the available scientific articles. In the experimental part, the effects of impurities with a high content of amorphous SiO2 on the rheological properties of fresh cement paste. It was tested by substitution of up to 10 % by weight of cement in the cement pastes mineral admixtures of different chemical composition, particle size and pozzolanic activity. Flow measurement was measured yield value, viscosity, and flow index. The stability of cement pastes was investigated oscillatory measurements. To complement the behavior pastes in the fresh state was determined by calorimetry. Test results were compared with those determined by reference samples and compared the effect of various ingredients.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:265357 |
Date | January 2017 |
Creators | Zimmermann, Štěpán |
Contributors | Rovnaník, Pavel, Vyšvařil, Martin |
Publisher | Vysoké učení technické v Brně. Fakulta stavební |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0017 seconds