Syntéza a vlastnosti keramických nanočásticových materiálů na bázi aniontově dopovaných kompozitních oxidů titanu / Synthesis and properties of ceramic nanoparticles based on anionic doped composite oxides of titanium

Master’s thesis deals with synthesis of anatase and its anion doping by carbo-nitridation. Prepared samples were used for testing of the photocatalytic activity. Low-temperature anatase was synthesized at 80 °C for 6 hours and carbo-nitridatation was carried out in ammonia/tetrachloromethane atmosphere at 500 °C for 3 hours. The influence of silver content on low-temperature crystallization of anatase was studied by reaction of titanium tetraisopropoxide with water. Silver nanoparticles were prepared by reduction of silver nitrate by D-glukose and sodium citrate. One of the results is the draft for one-pot synthesis of anatase by titanium tetraisopropoxide with complexing agent (sodium citrate, ammonium citrate, citric acid). The study of photocatalysis water splitting was carried out in the presence of 20 % vol. of methanol. Anatase prepared with citric acid has the highest photocatalytic activity (Pt 0,5 %) in UV/VIS spectral region. The activity achieved 38,6 % effectiveness of TiO2 standard (Degussa P25). Doping by nitrogen didn’t lead to increase of photocatalytic activity.

Identiferoai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216925
Date January 2013
CreatorsKašpárek, Vít
ContributorsVeselý, Michal, Cihlář, Jaroslav
PublisherVysoké učení technické v Brně. Fakulta chemická
Source SetsCzech ETDs
LanguageCzech
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/masterThesis
Rightsinfo:eu-repo/semantics/restrictedAccess

Page generated in 0.002 seconds