This dissertation reports the design of a process (patent pending) to remove iron from acid mine drainage (AMD) without the formation of metal hydroxide sludge. The system includes the oxidation of ferrous iron in a packed bed bioreactor, the precipitation of iron within a fluidized bed, the removal of manganese and heavy metals (Cu, Ni, Zn) in a trickling filter at high (>9) pH, with final neutralization in a carbonate bed. The technique avoided the generation of iron oxyhydroxide sludge.
In the packed bed bioreactor, maximum substrate oxidation rate (R<sub>,max</sub>) was 1500 mg L⁻¹ h⁻¹ at dilution rates of 2 h⁻¹, with oxidation efficiency at 98%. The half-saturation constant (similar to a Ks) was 6 mg L⁻¹. The oxidation rate was affected by dissolved oxygen below 2 mg L⁻¹, with a Monod-type Ko for DO of 0.33 mg L⁻¹. Temperature had a significant effect on oxidation rate, but pH (2.0 to 3.25) and supplemental CO₂ did not affect oxidation rates.
Iron hydroxide precipitation was not instantaneous when base was added at a OH/Fe ratio of less than 3. Induction time was found to be a function of pH, sulfate concentration and iron concentration, with a multiple R² of 0.84. Aqueous [Al (III)] and [Mn (II)] did not significantly (α = 0.05) affect induction time over the range of concentrations investigated.
When specific loading to the fluidized bed reactor exceeded 0.20 mg Fe m⁻² h⁻¹, dispersed iron particulates formed leading to a turbid effluent. Reactor pH determined the minimum iron concentration in the effluent, with an optimal at pH 3.5. Total iron removals of 98% were achieved in the fluidized bed with effluent [Fe] below 10 mg L⁻¹. Further iron removal occurred within the calcium carbonate bed.
Heavy metals were removed both in the fluidized bed reactor as well as in the trickling filter. Oxidation at pH >9 caused manganese to precipitate (96% removal); removals of copper, nickel, and zinc were due primarily to sorption onto oxide surfaces. Removals averaged 97% for copper, 70% for nickel and 94% for zinc.
The treatment strategy produced an effluent relatively free of iron (< 3 mg/L), without the formation of iron sludge and may be suitable for AMD seeps, drainage from acidic tailings ponds, active mine effluent, and acidic iron-rich industrial wastewater. / Ph. D.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/30713 |
| Date | 16 September 1997 |
| Creators | Diz, Harry Richard |
| Contributors | Civil Engineering, Novak, John T., Cherry, Donald S., Knocke, William R., Love, Nancy G., Rimstidt, J. Donald |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Dissertation |
| Format | application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | etd.pdf |
Page generated in 0.0021 seconds