With the use of photoluminescence (PL) spectroscopy one can able to get a
great deal of information about electronic structure and optical processes in
semiconductors by the aid of optical characterization. Among various compound
semiconductors, Cadmium Sulfide (CdS) and Gallium Selenide (GaSe) are
interesting materials for their PL emissions. Particularly, due to its strong anisotropy,
investigation of GaSe necessitates new experimental approaches to the PL technique.
We have designed, fabricated and used new experimental set-up for this purpose.
In this thesis, we have investigated the PL spectra of both CdS and GaSe as a
function of temperature. We observed interesting features in these samples. These
features were analyzed experimentally and described by taking the band structure of
the crystals into account. From the excitonic emissions, we determined the bandgap
energy of both materials. We studied various peaks that appear in the PL spectra and their origin in the material. We have found that donor acceptor transitions are
effective in CdS at low temperatures. A transition giving rise to a red emission was
observed and attributed to a donor level which is likely to result form an S vacancy
in CdS crystal. The PL peaks with energy close to the bandgap were observed in
GaSe. These peak were attributed to the bound excitons connected either to the direct
or indirect band edge of GaSe. The striking experimental finding in this work was the
PL spectra of GaSe measured in different angular position with respect to the crystal
axis. We observed that PL spectra exhibit substantial differences when the angular
position of the laser beam and the detector is changed. The optical anisotropy which
is responsible for these differences was measured experimentally and discussed by
considering the selection rules of the band states of GaSe.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/1258383/index.pdf |
| Date | 01 January 2003 |
| Creators | Seyhan, Ayse |
| Contributors | Turan, Rasit |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0021 seconds