Neste trabalho foram determinadas as condições para a soldagem de chapas grossas de aço carbono ASTM A36 com aço baixo-liga temperado e revenido ASTM A514 Grau Q empregando-se o processo arame tubular. Para tanto foram soldadas diversas peças de testes com o intuito de se avaliar as condições mais adequadas de preparação e soldagem de juntas dissimilares destes materiais. A preparação foi realizada por meio de corte térmico. A temperatura de preaquecimento foi determinada através de modelos matemáticos, pelas recomendações das normas AWS D1.1 e DIN EN 1011-2 sendo posteriormente avaliada por intermédio do teste de soldabilidade tipo CTS Controlled Thermal Severity. Os parâmetros de soldagem foram determinados a partir da qualificação de um procedimento de soldagem, conforme a norma AWS D1.1. Foram avaliadas as consequências do emprego do tratamento térmico de alívio de tensões após soldagem (TTAT), pelos testes de dureza Vickers e impacto Charpy. A caracterização microestrutural foi realizada por meio de microscopia óptica e microscopia eletrônica de varredura. A caracterização das superfícies oxicortadas evidenciou os efeitos da descarbonetação e também da carbonetação. A temperatura de pré-aquecimento de 160°C determinada por meio da metodologia recomendada pelas normas AWS D1.1 e DIN EN 1011-2 mostrou-se satisfatória nos testes de soldabilidade. Foi possível a qualificação do procedimento de soldagem (EPS) com requisitos de impacto na condição \"como soldado\", porém na condição \"após TTAT\", os baixos valores de tenacidade obtidos no metal de solda, inferiores a 27J, não permitiram a qualificação de uma EPS com requisitos de impacto. Foi observada a ausência de trincas intergranulares tanto na zona afetada pelo calor quanto no metal de base ASTM A514, porém foi revelada a presença de microfases frágeis no metal de solda na condição \"como soldado\", especificamente na região da raiz, intensificadas pelo efeito da diluição. O aumento do teor de carbono na raiz, a presença de microfases frágeis, a grande fração de grãos colunares e de ferrita proeutetóide combinados com a baixa fração de ferrita acicular no metal de solda contribuíram para os baixos valores de tenacidade encontrados na condição \"como soldado\". Após o TTAT observou-se uma queda acentuada da tenacidade, inferior a 27J, do metal de solda devido à fragilização provocada pela precipitação e coalescimento de carbonetos de ferro. / In this work it was determined the conditions for welding thick plate of ASTM A36 carbon steel with quenched and tempered low-alloy steel ASTM A514 Grade Q employing the Flux Cored Arc Welding (FCAW) process. For that several coupons of tests were welded in order to evaluate the most appropriate conditions for preparation and welding of these dissimilar materials. The preparation was carried out by means of thermal cutting. The preheat temperature was determined by mathematical models, the recommendations of standards AWS D1.1 and DIN EN 1011-2 being further evaluated using the CTS type weldability test - Controlled Thermal Severity. The welding parameters were determined by qualifying a welding procedure (WPS), according to AWS D1.1. The effects of post weld heat treatment (PWHT) were evaluated by Vickers hardness tests and Charpy. Microstructural characterization was performed by optical microscopy and scanning electron microscopy. The characterization of oxi-fuel cut surfaces showed the effects of decarburization and also carburization. The preheating temperature of 160 °C determined by calculation and the methodology recommended by the standards was satisfactory in weldability tests. It was possible qualification of welding procedure (WPS) with impact requirements in the condition \"as welded\" but the condition \"after PWHT\" low toughness values obtained in the weld metal, less than 27J, did not allow to qualify a WPS with toughness requirements. The absence of intergranular cracking was observed in both the heat affected zone as the base metal ASTM A514, but the presence of fragile microphase in the weld metal was revealed in the weld metal in the condition \"as welded\" specifically in the root region, intensified by the effect of dilution. The carbon increase at root, the presence of fragile microphase, the large fraction of columnar grains and proeutectoid ferrite combined with the low fraction of acicular ferrite in the weld metal contributed to the low toughness values found in the condition \"as welded \". After PWHT there was a sharp drop in toughness, less than 27J, in the weld metal due to embrittlement caused by precipitation and coarsening of iron carbides.
| Identifer | oai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-31032017-141554 |
| Date | 09 December 2016 |
| Creators | Marcello Ferrari |
| Contributors | Maurício David Martins das Neves, José Roberto Berretta, Volodymyr Ponomarov |
| Publisher | Universidade de São Paulo, Tecnologia Nuclear, USP, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds