Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T01:37:33Z (GMT). No. of bitstreams: 1
Guedes-Pinto_Eduardo_M.pdf: 2855830 bytes, checksum: ffca1786148a3514f02f16d72b6577e2 (MD5)
Previous issue date: 1997 / Resumo: A proposta deste estudo foi avaliar a resistência ao cisalhamento de três materiais de colagem, polimerizados por diferentes sistemas de ativação. Foram utilizados 60 pré-molares humanos, extraídos com finalidade de tratamento ortodôntico. As faces vestibulares foram condicionadas com ácido fosfórico a 37% durante 30 segundos e os bráquetes fixados ao esmalte dentário com as . resinas Concise Ortodôntico (3M), Z-100 (3M) e cimento resinoso Dual (3M). Após a fixação dos bráquetes metálicos, os corpos-de-prova foram submetidos ao teste de cisalhamento 10 minutos e 24 horas após as colagens. Os resultados submetidos à análise estatística mostraram que houve diferença estatisticamente significante entre os três tipos de resina para os dois períodos de tempo de armazenamento. O sistema de colagem mais resistente foi promovido pelo Concise Ortodôntico, seguido pela resina fotoativada Z-100, e o menos resistente foi o cimento resinoso Dual. O tempo de armazenamento foi estatisticamente significante, pois representou aumento na resistência ao cisalhamento nos três tipos de materiais, provavelmente, devido à contínua conversão dos radicais livres / Abstract: The purpose of this study was to evaluate the shear bond strengths of three bonding materiaIs, activated by different systems. Sixty human premolars, extracted for orthodontic reasons, were used. Vestibular faces were etched for 30 seconds with 37% phosphoric acid gel and brackets were bonded to enamel surface using Concise chemically cured adhesive (3M), Z-100 light-cured adhesive (3M) and Dual cemerit resin (3M). After the bonding of metal brackets, specimens were tested and the shear stress at bond failure was recorded at 10 minutes and 24 hours. Results submitted to statistical analysis demonstrated a statistically significant difference in shear bond strengths among the three resins for both periods of storage. The most resistant bonding system was the Concise group, followed by the light-cured Z-100 and the less resistant Dual cement resin. The storage was statistically significant by increasing the shear bond strengths of the three materiaIs, probably because of the continue conversion / Mestrado / Ortodontia / Mestre em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290087 |
Date | 27 November 1997 |
Creators | Guedes-Pinto, Eduardo |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Nouer, Darcy Flávio, Ferreira, Flávio Vellini |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Ciências |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 97f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |