Previous issue date: 2015-03 / Este trabalho se propõe a contribuir com o desenvolvimento de técnica não
destrutiva com o objetivo de garantir a integridade estrutural de componentes
nucleares. Foi realizada uma avaliação acustoelástica do aço 20 MnMoNi 55,
utilizado em vasos de pressão de usinas nucleares. A técnica da birrefringência
acústica foi empregada para avaliar o comportamento acustoelástico do material em
estudo como recebido, após a soldagem e posteriormente ao tratamento térmico de
alívio de tensões. A constante acustoelástica do material foi obtida por ensaio de
carregamento uniaxial. Foi verificada uma leve anisotropia no material como
recebido. Após a soldagem foi observada uma acentuada variação da birrefringência
acústica na região próxima ao cordão de solda. O tratamento térmico indicou uma
nova alteração da birrefringência acústica. A obtenção da constante acustoelástica
permitiu a avaliação de tensão nas diferentes condições do material soldado e
tratado. / This paper aims to contribute to the non-destructive technique development in order
to ensure the structural integrity of nuclear components. One acoustelastic evaluation
of steel 20 MnMoNi 55, used in pressure vessels of nuclear power plants was
performed. The acoustic birefringence technique was used to evaluate the
acoustelastic behavior of the test material in the as received condition, after welding
and after the stress relief heat treatment. The constant acoustelastic material was
obtained by an uniaxial loading test. It was found a slight anisotropy in the material
as received. After welding, a marked variation of acoustic birefringence in the region
near the weld bead was observed. The heat treatment indicated a new change of
acoustic birefringence. Obtaining the acoustelastic constant allowed the evaluation of
stress in the different conditions of the weld and treated material.
| Identifer | oai:union.ndltd.org:IBICT/oai:carpedien.ien.gov.br:ien/1458 |
| Date | 03 1900 |
| Creators | MORAES, Bruno Cesar de |
| Contributors | JOSPIN, Reinaldo Jacques, PAYÃO FILHO, João da Cruz, BITTENCOURT, Marcelo de Siqueira Queiroz |
| Publisher | Instituto de Engenharia Nuclear, Programa de Pós-graduação em Ciência e Tecnologia Nucleares, IEN, Brasil, Instituto de Engenharia Nuclear |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional do IEN, instname:Instituto de Engenharia Nuclear, instacron:IEN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds