Desempenho de embalagens metalicas para bebidas carbonatadas : avaliação de latas fabricadas por soldagem eletrica frente as latas convencionais

Orientador : Pilar R. de Massaguer / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-07-14T19:10:10Z (GMT). No. of bitstreams: 1
Dantas_SilviaTondella_M.pdf: 23016877 bytes, checksum: 1f8bba3fc4ceaa278da37d6dca23793d (MD5)
Previous issue date: 1987 / Resumo: Avaliou-se o desempenho de quatro tipos de latas, sendo duas produzidas por tecnologias de soldagem elétrica Soudronic e Conoweld e duas pelo processo convencional (solda Sn/Pb), Com exceção da lata produzida pelo processo Conoweld, que foi fabricada em folha cromada, o material de embalagem foi a folha-de-flandres. Todas as latas eram envernizadas internamente. O produto estudado foi refrigerante de limão. A vida-de-prateleira do produto nas diversas embalagens foi determinada em teste de estocagem óelo período de seis meses em duas condições de temperatura, 23ºC e 35ºC. Os principais parâmetros considerados foram a avaliação visual interna das embalagens, a concentração de ferro e a avaliação organoléptica do produto. Verificou-se que, embora apresentem pequenas diferenças entre si, todos os tipos de latas de folha-de-flandres (soldadas pelo processo convencional e eletricamente) apresentaram um bom desempenho pelos seis meses de estocagem, enquanto a lata em folha cromada soldada eletricamente sofreu um processo de corrosão acentuado, e o produto nela acondicionado atingiu concentrações de ferro acima do admissível (2ppm aos seis meses de estocagem) entre 90 e 120 dias no armazenamento a 23ºC e entre 75 e 90 dias no armazenamento a 35ºC. Para a estocagem a 23ºC esse foi o tempo estabelecido para a vida-de-prateleira do produto nessa embalagem enquanto para a estocagem a 35ºC a vida-de-prateleira estabelecida foi entre 62 e 75 dias devido ao sabor metálico percebido na avaliação sensorial. A avaliação sensorial do refrigerante de limão permitiu verificar a ocorrência de deterioração do sabor do produto durante a estocagem, nas duas condições de temperatura, ocorri da no produto acondicionado nos diversas tipos de embalagem metálica e também na garrafa de vidro utilizada como referencia. Em função disso, o fator limitante da vida-de-prateleira do refrigerante de limão nas embalagens em folha-de-flandres foi a alteração organoléptica, sendo o produto considerado inaceitável aos 150 dias de estocagem a 23ºC e 105 dias de estocagem a 35ºc. A caracterização das embalagens quanto à porosidade do verniz e proteção da região de soldagem mostrou-se diretamente relacionada as diferenças no desempenho encontradas entre as embalagens. A avaliação de amostras da região de soldagem no tempo zero e aos 180 dias de estocagem a 23ºC por meio de microscopia eletrônica e difração de raiosX possibilitou a visualização e confirmação da formação de pontos de corrosão e existência de defeitos no sistema de envernizamento das embalagens. / Abstract: The performance of four kinds of cans, two of them produced by Soudronic and Conoweld welding technologies, and the other two by the conventional process (soldered), was evaluated. With the exception of the can produced by the Conoweld process that was manufactured from tin free steel, the packaging material was tinplate. All of the cans were lacquered internally. The product studied was a lemon soft drink. The shelf-life of the product in the several packagings was determined by storage test within a period of six months at two temperature conditions, 23ºC and 35ºC. The main parameters considered were the internal visual evaluation of the packaging, the concentration of iron and the sensorial evaluation of the product. It was verified that although the tinplate cans presented some small differences among them selves, all of the types of tinplate cans (welded and soldered) presented a good performance during the six months of storage, while the welded tin free steel can suffered a process of accentuated corrosion and the product packaged in it reached concentrations of iron above the permissible tolerance (2ppm at six months of storage) between 90 and 120 days in storage at 23ºC and between 75 and 90 days in storage at 35ºC. For the storage at 23°C, that was the period established for the shelf-life of the product in this packaging, while for the storage at 35°C the shelf-life was between 62 and 75 days in function of the metallic flavor detected in the sensorial evaluation. The sensorial evaluation of the lemon soft drink allowed us to detect the product flavor deterioration during the storage at the two temperature conditions that occured in the product packaged in several types of metalic packaging and also in glass used as reference. In function of that, the limitating factor of the shelf--life of the lemon soft drink in tinplate packagings was the sensorial alteration. The product was considered unacceptable at 150 days of storage at 23ºC and at 105 days of storage at 35ºC. The caracterization of the packagings as to lacquer porosity and protection of the region of welding proved to be directly related to the differences in performance verified among the packagings. The evaluation of samples of the region of welding at time zero and at 180 days of storage at 23°C in Scanning Electron Microscope and X-Ray Diffraction enabled the visualization and confirmation of points of corrosion formation and the existence of defects in the system of packaging lacquering. / Mestrado / Mestre em Ciência de Alimentos

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/255379
Date12 August 1987
CreatorsDantas, Silvia Tondella
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Rodriguez de Massaguer, Pilar, 1947-, Massaguer, Pilar Rodriguez de, 1947-
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia de Alimentos, Programa de Pós-Graduação em Ciência de Alimentos
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format285f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.002 seconds