This research investigates the use of conducting polymer coatings on platinum (Pt) electrodes for use in neuroprostheses. Conducting polymers aim to provide an environment conducive to neurite outgrowth and attachment at the electrode sites, producing intimate contact between neural cells and stimulating electrodes. Conducting polymers were electropolymerised onto model Pt electrodes. Conventional polymers polypyrrole (PPy) and poly-3,4-ethylenedioxythiphene (PEDOT) doped with polystyrenesulfonate (PSS) and para-toluenesulfonate (pTS)were investigated. Improvement of material properties was assessed through the layering of polymers with multi-walled carbon nanotubes (MWNTs). The ability to incorporate cell attachment bioactivity into polymers was examined through the doping of PEDOT with anionic laminin peptides DCDPGYIGSR and DEDEDYFQRYLI. Finally, nerve growth factor (NGF), was entrapped in PEDOT during polymerisation and tested for neurite outgrowth bioactivity against the PC12 cell line. Each polymer modification was assessed for electrical performance over multiple reduction-oxidation cycles, conductivity and impedance spectroscopy, mechanical adherence and hardness, and biological response. Scanning electron microscopy was used to visualise film topography and x-ray photon spectroscopy was employed to examine chemical constitution of the polymers. For application of electrode coatings to neural prostheses, optimal bioactive conducting polymer PEDOT/pTS/NGF was deposited on electrode arrays intended for implantation. PC12s were used to assess the bioactivity of NGF functionalised PEDOT when electrode size was micronised. Flexibility of the design was tested by tailoring PEDOT bioactivity for the cloned retinal ganglion cell, RGC-5, differentiated via staurasporine. It was established that PEDOT films had superior electrical and cell growth characteristics, but only PPy was able to benefit from incorporation of MWNTs. Bioactive polymers were produced through inclusion of both laminin peptides and NGF, but the optimum film constitution was found to be PEDOT doped with pTS with NGF entrapped during electrodeposition. Application of this polymer to an implant device was confirmed through positive neurite outgrowth on vision prosthesis electrode arrays. The design was shown to be flexible when tailored for RGC-5s, with differentiation occurring on both PEDOT/pTS and PEDOT/DEDEDYFQRYLI. Conducting polymers demonstrate the potential to improve electrode-cell interactions. Future work will focus on the effect of electrical stimulation and design of bioactive polymers with improved cell attachment properties.
| Identifer | oai:union.ndltd.org:ADTP/205412 |
| Date | January 2009 |
| Creators | Green, Rylie Adelle, Graduate School of Biomedical Engineering, Faculty of Engineering, UNSW |
| Publisher | Publisher:University of New South Wales. Graduate School of Biomedical Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://unsworks.unsw.edu.au/copyright, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0021 seconds