Orientadores: Mário Alexandre Coelho Sinhoreti. Americo Bortolazzo Correr / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T04:06:35Z (GMT). No. of bitstreams: 1
Abuna_GabrielFlores_M.pdf: 32440601 bytes, checksum: 93c6f8fada4bccad124db9dc6ea6c205 (MD5)
Previous issue date: 2015 / Resumo: Objetivos: O objetivo no presente trabalho foi avaliar o potencial remineralizador e a as propriedades adesivas (resistência de união, análise das interfaces, nanoinfiltração) de um novo sistema adesivo baseado em fosfatos e dois análogos biomiméticos incorporados em um adesivo experimental autocondicionante de dois passos. Métodos: Foi preparado um primer-base, onde foram incorporados os análogos e um adesivo-base contendo os fosfatos. Para avaliar o potencial remineralizador foram desmineralizadas barras de dentina (n=5) (EDTA 17%), distribuídas em: Controle sem análogos e sem fosfatos; Primer+Fosfatos; Acido poliacrilico APA+Fosfatos; Trimetafosfato de sódio TMS+Fosfatos; e Analogos+fosfatos. tratadas com cada primer e fixados junto a uma barra do adesivo polimerizado, em 1,5 mL de solução fosfato tampão. Foi usado um Espectroscópio Infravermelho Transformado de Fourier (ATR-FTIR) para caracterizar os fosfatos formados. Os espectros foram obtidos depois das 24 h, 7 dias, 2 e 6 meses. Microscopia Eletrônica de Transmissão (MET) foi usada para avaliar a interação dos cristais de apatita com o colágeno. Para avaliar as propriedades adesivas 50 dentes molares humanos hígidos foram usados (n=5): O primer foi aplicado por 10 segundos e o adesivo por 20 segundos, seguido de fotoativação por 20 s. Após, foram restaurados (Filtek Z350) em incrementos de 2 mm. Após 24 h ou 6 meses de pressão pulpar simulada (PPS), os dentes foram cortados em palitos de 0.9 x 0.9 mm2 e foi testada a resistência da união (EZ-test; Shimadzu, Kyoto, Japan), analisado o modo de fratura em estereomicroscópio. Um palito por dente foi selecionado e avaliado no ensaio nanoinfiltração, usando nitrato de prata amoniacal. Ainda, foi selecionado um palito por dente para avaliar a camada híbrida em Microscópio Eletrônico de Varredura com 15 KV. O analise estatístico da resistência de união foi feita com teste ANOVA dois fatores, e normalizados com Teste de Tukey, (p<0.05) Resultados: Todos os espetros do ATR-FTIR foram normalizados em 1650 cm-1 Amida I. Foi observado após 6 meses de PPS, a presença de picos em 947 e o par em 1092 cm-1 atribuídos a união C=O da HAp, e picos de PO4 em 1033 cm-1 , além de outros picos representativos da HAp. A análise em MET mostrou que, sem a intervenção dos análogos, a mineralização só ocorre nos espaços extrafibrilares, contrário a imagem com ambos análogos, onde observou-se uma organização em forma de agulhas intrafibrilar das apatitas. A resistência de união demostrou como a presença dos análogos e fosfatos não atrapalhou a adesão mostrando uma resistência similar no grupo de Analogos+Fosfatos, comparando-se 24 h com 6 meses de PPS (35,12±5,16 MPa e 38,67 ±4,03 MPa, respectivamente). No MEV observou-se a qualidade da camada adesiva, mostrando os túbulos dentinários obstruídos após 6 meses de PPS. Após a análise da nanoinfiltração, observou-se que a sorção de água diminui proporcionalmente à mineralização do grupo Analogos+Fosfatos. Conclusão: O sistema remineralizador proposto formou núcleos de HAp caracterizados mediante o ATR-FTIR, alcançando zonas intrafibrilares do colágeno, e mantendo o desempenho do adesivo após armazenamento em pressão pulpar simulada / Abstract: Objective: The aim of this study was to assess the remineralization potential and bonding properties of a novel system based on phosphates and biomimetic analogs incorporated into a two-step self-etch adhesive. Methods: It was prepared a main primer where were added the analogs and one main blend where were incorporated the phosphates. To assess the remineralization properties, to assess the mineral deposition dentin slabs were (n=5) demineralized (EDTA 17%), treated in each primer and fixed next to a polymerized adhesive slab (Under 1.5 mL phosphate buffer solution). It was used an ATR-FTIR to characterize the new phosphates. The spectra were recorded after 24 hrs, 7 days, 2 months and 6 months. The Transmission electronic microscopy was used to assess the nanometric interaction of apatite crystals and demineralized dentin collagen. In order to assess Dentin bonding properties, 50 non-carious human molars were used. (Under 038/2014 CEP-FOP protocol) divided into 5 groups n=10: PAA+Phosphates- polyacrylic acid-containing primer and phosphates-doped bond; STMP+Phosphates- Sodium trimetaphosphate-containing primer and phosphates-doped bond; Analogs+Phosphates- both analogs in the primer and phosphates-doped bond. The primer was applied for 10 s, the adhesive was applied for 20 s and light cured for 20 s. Then were resin (Filtek z350) restored at 2 mm layers. After 24 hrs or 6 months of simulated pulpal pressure SPP, the teeth were sectioned in sticks of 0.9 mm2 tested the µTensile Bond Strength, and analyzed the failure mode at a stereomicroscope. One stick per teeth was chosen and assessed Nanoleakage, using ammoniacal silver nitrate solution to reveal the hybrid layer at a Scanning Electronic Microscopy. Results: All the spectra of ATR-FTIR were normalized at 1650 Amide I. It was observed after 6 months of SPP, the presence of peaks at 947 and its pair at 1092 cm-1 attributed to C=O of HAp, and peaks of PO4 at 1033 cm-1 besides other specific peaks that confirm the presence of HAp. The TEM analysis showed, without the intervention of analogs the mineralization occurs just at in the extrafibrilar spaces, opposite to the image with both analogs where it is showed an intrafibrilar organization of needles like apatites. The µTBS outcomes demonstrate how the presence of this analogs and phosphates did not jeopardize the bonding strength. Showing a µTBS similar at Analogs+Phosphates, comparing 24 hrs of SPP to 6 months of SPP (35.12+5.16 MPa and 38.67 +4.03 MPa) (?=0.05). With SEM we observed the quality of this adhesive layer, showing occluded tubules after 6 months of SPP and no degradation of Resin tags. After Nanoleakage evaluation we see how after remineralization the water income decrease proportional to the mineralization. Conclusion: The proposed remineralizing system nucleate HAp characterized by ATR-FTIR in this study. Achieving the intrafibrilar zones of collagen, and keeping the performance of the adhesive after storage under SPP, maintaining the bonding properties and decreasing the factors of common adhesive degradation / Mestrado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288144 |
| Date | 27 August 2018 |
| Creators | Abuna, Gabriel Flores, 1989- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Correr, Americo Bortolazzo, 1981-, Sinhoreti, Mário Alexandre Coelho, 1969-, Goes, Mario Fernando de, Ogliari, Fabrício Aulo |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 38 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds