Previous issue date: 2015-08-26 / Capes / As indústrias do beneficiamento de rochas ornamentais, da cerâmica vermelha e do caulim, geram grande volume de resíduos, que geralmente são dispostos no meio ambiente de forma inadequada, causando graves impactos ambientais. A reinserção de resíduos industriais na cadeia produtiva como matéria prima, no desenvolvimento de insumos da construção, vem sendo uma alternativa avaliada por diversos pesquisadores. Os resultados de pesquisas apontam que estes resíduos, quando beneficiados podem apresentar propriedades aglomerantes que viabilizam sua incorporação em substituição parcial à cal na confecção de blocos solo-cal. Dentre os materiais alternativos, o bloco solo-cal possui vantagens como simplicidade de produção, resistência à compressão semelhante aos blocos convencionais, não passam pelo processo de cozimento e possibilitam a incorporação de resíduos com potencial aglomerante à sua matriz. Porém para assegurar confiabilidade nas aplicações desses novos materiais, é fundamental a avaliação da durabilidade. Este trabalho de pesquisa teve como objetivo avaliar a durabilidade de blocos solo-cal incorporados com resíduos industriais provenientes do beneficiamento de rochas ornamentais, da fabricação da cerâmica vermelha e do beneficiamento do caulim. Confeccionaram-se blocos no traço 1:10 em proporção de cal:solo, e utilizando os resíduos em substituição parcial a cal, nas proporções de 15%, 30% e 50% para períodos de cura de 28, 60 e 90 dias. Os materiais utilizados foram submetidos aos ensaios de caracterização físico-mineralógica, tais como:granulometria por peneiramento e difração a laser, análise química, análise
termodiferencial, análise termogravimétrica, e difração de raios X. O estudo da
durabilidade foi realizado utilizando-se o envelhecimento natural, o envelhecimento acelerado pela técnica de molhagem e secagem , simulação da chuva dirigida e
resistência ao ataque de sulfatos, tomando-se como parâmetro de degradação a
resistência à compressão simples dos blocos. Os resultados evidenciaram que a
incorporação de 15% de resíduo cerâmico e de caulim ao bloco solo-cal não
compromete sua durabilidade. / The industries of beneficiation of ornamental rocks, red ceramic and kaolin,
generate large volume of waste, which are mostly discharged into the environment
irregularly, thus causing serious environmental impacts. The reintegration of
industrial waste in the productive chain, as raw material in the development for
building materials, are being an alternative evaluated by several researchers. Among
the alternative materials, soil-lime blocks has advantages such as simplicity of
production, compression resistance similar to conventional blocks, are not submitted
to the cooking process and enable the incorporation of waste with potential binder to
matrix. Research results indicate that these residues when finely ground may submit
caking properties that enable its incorporation in partial substitution of lime in soillime blocks manufacture. But to ensure reliability to alternative materials is essential
evaluating their durability. This research aimed to evaluate the durability of soil-lime
blocks incorporated with industrial waste arising from the processing of ornamental
rocks, manufacturing of red ceramic and kaolin. Specimens were made at the dash
1:10 in ratio of lime: soil, and using waste to partially replace lime in the proportions
15%, 30% and 50% for curing periods of 28, 60 and 90 days. The materials were
subjected to physical and mineralogical characterization tests, such as: granulometry
by sieving and laser diffraction, chemical analysis, thermo differential analysis,
thermo gravimetric analysis, and X-ray diffraction. The study of the durability was
performed using the natural aging, accelerated aging by the technique of wetting and
drying, driving rain simulation and resistance to attack sulfates , taking as parameter
degradation the unconfined compressive strength of the blocks. The results showed
that the incorporation of 15% ceramic waste and kaolin in soil -lime block does not
compromise its durability.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1049 |
| Date | 26 June 2018 |
| Creators | FIGUEIREDO, Suélen Silva. |
| Contributors | NEVES, Gelmires de Araújo., FERREIRA, Heber Carlos., LUCENA , Leda Christiane de Figueiredo Lopes., SEVERO, Cibele Guimarães Silva., FERREIRA, Heber Sivini., OLIVEIRA, Djane de Fátima. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds